Abstract:SrO–BaO–B2O3–SiO2 glass-ceramics with a high dielectric constant and low dielectric loss were prepared. The influence of the SiO2/BaO ratio on the sintering behavior, crystallization behavior, and properties were systematically investigated. The results showed that the increasing amount of liquid phase from increasing the SiO2/BaO ratio promoted sintering, resulting in an initial decrease in the sintering activation energy. However, the viscosity of the liquid phase continued to increase, leading to an increase in the sintering temperature and sintering activation energy when the SiO2/BaO ratio reached 0.90. As the SiO2/BaO ratio increased, the fraction of the primary phase BaSi2Al2O8 increased, and its grains grew; the minor phase SrTiO3 was suppressed, resulting in changes in the properties of the glass-ceramics. The sample with a SiO2/BaO ratio of 0.69, which was sintered at 850 °C for 10 min, showed excellent properties: a coefficient of thermal expansion (CTE) of 10.63 × 10−6 K−1 (25–500 °C), a dielectric constant (ϵr) of 16.24 (1 MHz), a dielectric loss (tanδ) of 3.39 × 10−3 (1 MHz), a flexural strength of 138.80 MPa, and a quality loss of acid corrosion of 1.06 × 10−4 g mm−2. The results indicated that the SrO–BaO–B2O3–SiO2 glass-ceramics used in this study have great potential for low-temperature co-fired ceramics applications.

Low temperature preparation of the β-CaSiO3 ceramics based on the system CaO–SiO2–BaO–B2O3

Low Temperature Preparation of the Zn 2 SiO 4 Ceramics with the Addition of BaO and B 2 O 3

Preparation and properties of low temperature sintered CaO-B 2 O 3 -SiO 2 microwave dielectric ceramics using the solid-state reaction

Synthesis of a low-firing BaSi2O5 microwave dielectric ceramics with low dielectric constant

Microstructure, Thermal, Mechanical, and Dielectric Properties of BaO-CaO-Al2O3-B2O3-SiO2 Glass-Ceramics

Microstructure and Properties of ZrO 2 -, TiO 2 -Doped Ca–Si–B Based Ceramics

Effects of B2O3 content on crystallization behavior and properties of low temperature co-fired CaO-B2O3-SiO2 glass-ceramics

Microstructure, Thermal, Mechanical, and Dielectric Properties of BaO–CaO–Al2O3–B2O3–SiO2 Glass-Ceramics

Effect of SiO2/BaO ratio on sintering behavior, crystallization behavior, and properties of SrO–BaO–B2O3–SiO2 glass-ceramics

Low Temperature Sintering and Dielectric Properties of BaTi_(0.75)Zr_(0.25)O_3 Ceramic

Low-Temperature Preparation and Electrical Properties of Cabi2nb2o9 Piezoelectric Ceramic by Addition of B2o3

Pseudo low-temperature sintering effect and microstructure evolution of SiBCO ceramics

Low-Temperature Sintering and Microwave Dielectric Properties of Ba2Ti9O20 Ceramics with CaO–B2O3–ZnO Glass Additions

Densification and Dielectric Properties of CaO–B2O3–SiO2 System Glass Ceramics

Low-temperature sintering kinetics and dielectric properties of Ba5Nb4O15 with B2O3–SiO2 glass

Effects of B2O3 Contents on Crystallization Behaviors and Dielectric Properties of CaO-B2O3-SiO2 Glass Ceramics

Low-temperature sintering and microwave dielectric properties of Ca2Zn4Ti15O36 ceramics

Low temperature sintering and microwave dielectric properties of BaO–0.6ZnO–2.9TiO 2 ceramics using BaCu(B 2 O 5 ) addition

Influence of Al 2 O 3 /SiO 2 ratio on the microstructure and properties of low temperature co-fired CaO–Al 2 O 3 –SiO 2 based ceramics

Effect of Ca/Si ratio on the microstructures and properties of CaO–B2O3–SiO2 glass-ceramics

Effects of B<sub>2</sub>O<sub>3</sub> Contents on Crystallization Behaviors and Dielectric Properties of CaO-B<sub>2</sub>O<sub>3</sub>-SiO<sub>2</sub> Glass Ceramics