Effect of Welding Parameters on Solidification Cracking in Butt Weld Roots of SA335 P91 Pipes

HUANG Si-luo,ZHANG Jian-xun,NIU Jing,CHEN Zong-qiang

DOI: https://doi.org/10.3969/j.issn.1000-7466.2006.01.002

2006-01-01

Abstract:Key welding parameter that influence the susceptive of solidification cracking in the butt weld roots of SA335 P91 pipes are studied in the method of orthonormal test.The experimental result shows that the welding current and the holding time to close the seam joint are two significant factors in the cracking cases,whereas holding time contributes more to the final results.According to the technical analysis of the close joint by metallography,stereoscan and energy spectrum,long holding time and great welding current cause coarse lath martensite with intensive directivity and serious intergranular aliquation of low melting point sulfur eutectic.Solidification cracking is determined by the distribution of the low melting sulfur eutectic other than the content of sulfur itself.When sulfur content is high,the close joint is more likely subject to solidification cracking with sulfide films and blocks concentrating along the grain boundaries.