Investigation on solidification crack susceptibility for weld metals of GH3539 alloy with Trans-Varestraint test

Jintao Tian,Shuangjian Chen,Chengpeng Liu,Guanhong Lei,Shuai Yan,Xiang-Xi Ye

DOI: https://doi.org/10.1016/j.mtcomm.2024.110898

IF: 3.8

2024-11-07

Materials Today Communications

Abstract:In this work, the welding solidification crack susceptibility of GH3539 alloy was investigated under different strains using a trans-varestraint test. The results indicate that the saturation strain of GH3539 alloy reaches a bending strain of 1 %. High-angle grain boundaries in the weld metal are fragile areas where welding solidification cracks are formed due to element segregation and stress concentration, which are essential factors causing crack initiation and propagation. Furthermore, the surface residual stress of the crack tip was calculated by two-dimensional synchronous micro X-ray diffraction analysis of the partial Debye ring, which was deduced as the major factor for the cracking. The element Si in the alloy tends to segregate at grain boundaries, forming low-melting liquid films with elements such as Mo, Cr, and Mn during the final solidification stage. These liquid films reduce the interfacial bonding strength at the grain boundaries. The failure of the liquid films to accommodate local stress, resulting in subsequent interface separation, serves as the other catalyst for initiating solidification cracks in welding.

materials science, multidisciplinary