Abstract:Characterization of the damage behavior and failure mechanisms of the bonded‐bolted hybrid three‐bolt joint in composite laminates by a combined experimental and finite element approach. In this paper, the mechanical properties, damage modes, and bolt load distribution of the bonded‐bolted hybrid three‐bolt joint were investigated by a combination of experiments and numerical simulations. Acoustic emission (AE) was used to monitor the tensile process of the connection in real time, and the K‐means clustering algorithm was used to realize the cluster analysis of the damage modes. A numerical simulation model of the tensile process of the joint was established using ABAQUS simulation software. The progressive damage evolution of composite laminates, and adhesive layer was characterized by using the VUMAT subroutine, the B‐K failure criterion, and cohesive element with zero thickness, respectively. The results show that four main damage modes occur in composite laminates during tension: matrix cracking, delamination, fiber pull‐out, and fiber breakage, with corresponding peak frequency ranges of (0–80 kHz), (80–210 kHz), (210–330 kHz), and (330–375 kHz), respectively. The adhesive layer between the laminates mainly exhibits peeling failure because of the secondary bending effect. In the load‐bearing process, the adhesive layer was loaded first and failed, and the bolt loading was delayed. Meanwhile, the results of bolt load distribution showed that the bolts and the adhesive layer at both ends carried greater loads. Highlights Damage modes and damage evolution of the bonded‐bolted hybrid joint in tension were analyzed by combining acoustic emission technology and numerical simulation. The simulation of delamination damage in composite laminates was carried out by inserting zero‐thickness cohesive elements into the laminates, and the delamination damage between the carbon fiber layup and the adjacent glass fiber layup was analyzed. The effect of the inclusion of the adhesive layer on the mechanical properties of the joint and the distribution of the bolt load was analyzed.

STUDY ON TENSION PROPERTIES OF HYBRID-LAMINATED PLAIN WOVEN FABRIC COMPOSITE WITH SINGLE BOLT JOINT

On Numerical Modeling and Tensile Strength of Bolted Composite Joints

Experimental and Numerical Study on Bearing Failure of Countersunk Composite–composite and Composite–steel Joints

Numerical and experimental investigation on the load‐bearing performance of plain‐woven composites hybrid bonded‐bolted joints

TENSILE PERFORMANCE ANALYSIS OF COMBINED ADHESIVE AND BOLTED JOINTS FOR PLAIN WOVEN COMPOSITES

Fatigue Behaviour and Failure Mechanism of the Thin/thick-Ply Hybrid Laminated Composite Bolted Joints

The Failure Analysis of Composite Bolted Joint Structure Based on a Nonlinear Model

An engineering approach to predict the bearing strength of single-bolted double-lapped joints in composite laminate

Analysis of the Bonded-bolted Hybrid Composite Joints' Strength and Influences

Investigation on the Progressive Damage and Bearing Failure Behavior of Composite Laminated Bolted Joints under Tension

SIMULATION OF COMPRESSIVE FAILURE OF HYBRID PLAIN WOVEN FABRIC LAMINATE WITH A HOLE

Strength and damage evolution of mid-thick composite laminates with countersunk bolt joints

Analysis of the Influence Factors on the Mechanical Properties of Single-bolted Composite Laminates

Assessment of Tensile Behavior and Failure Mechanism in the Two Integrated Composite Joints

Parametric study on the load-carrying capacity of plain-woven composites hybrid bonded-bolted joints

Failure Behavior Of Plain Weave Fabric Composite With Bolted Joints

INTERLAMINAR STRESS ANALYSIS OF COMPOSITE LAMINATES SUBJECTED TO IN-PLANE LOADING

Damage Investigation and Design of Woven Composite Bonded Joint

A Bi-Material Property Based FE Modelling Method for Progressive Damage Analyses of Composite Double-Lap Bolted Joints

Numerical Analysis on Tensile Properties of Composite Hybrid Bonded/bolted Joints with Flanging

Characterization of damage behavior and failure mechanisms of the bonded‐bolted hybrid three‐bolt joint in composite laminates