Abstract:The friction and wear properties of the polyetheretherketone (PEEK) based composites filled with 5 mass% nanometer or micron Al2O3 with or without 10 mass% polytetrafluroethylene (PTFE) against the medium carbon steel (AISI 1045 steel) ring under the dry sliding condition at Amsler wear tester were examined. A constant sliding velocity of 0.42ms−1 and a load of 196 N were used in all experiments. The average diameter 250μm PEEK powders, the 15 or 90nm Al2O3 nano-particles or 500nm Al2O3 particles and/or the PTFE fine powders of diameter 50μm were mechanically mixed in alcohol, and then the block composite specimens were prepared by the heat compression moulding. The homogeneously dispersion of the Al2O3 nano-particles in PEEK matrix of the prepared composites was analyzed by the atomic force microscopy (AFM). The wear testing results showed that nanometer and micron Al2O3 reduced the wear coefficient of PEEK composites without PTFE effectively, but not reduced the friction coefficient. The filling of 10 mass% PTFE into pure PEEK resulted in a decrease of the friction coefficient and the wear coefficient of the filled composite simultaneously. However, when 10 mass% PTFE was filled into Al2O3/ PEEK composites, the friction coefficient was decreased and the wear coefficient increased. The worn scars on the tested composite specimen surfaces and steel ring surfaces were observed by scanning electron microscopy (SEM). A thin, uniform, and tenacious transferred film on the surface of the steel rings against the PEEK composites filled with 5 mass% 15nm Al2O3 particles but without PTFE was formed. The components of the transferred films were detected by energy dispersive spectrometry (EDS). The results indicated that the nanometer Al2O3 as the filler, together with PEEK matrix, transferred to the counterpart ring surface during the sliding friction and wear. Therefore, the ability of Al2O3 to improve the wear resistant behaviors is closely related to the ability to improve the characteristics of the transfer film.

Influence of Al2O3 reinforcement on the abrasive wear characteristic of Al2O3/PA1010 composite coatings

Abrasive wear characteristics and mechanisms of A12O3/PA1010 composite coatings

Fabrication and performance of Ni-Co-P/Si3N4 electroplated composite coatings on al-si alloys

Microstructure and Tribocorrosion Behavior of Al2O3/Al Composite Coatings: Role of Al2O3 Addition

FABRICATION OF Al2O3/HEAT-RESISTANT STEEL COMPOSITEAND ITS WEAR-RESISTANCE AT HIGH TEMPERATURE AND ABRASIVE

Dry Sliding Wear Behaviour of Al<sub>2</sub>O<sub>3</sub>-Cr<sub>2</sub>O<sub>3</sub> Coatings with Different Contents of Cr<sub>2</sub>O<sub>3</sub>

A study on friction and wear characteristics of nanometer Al2O3 /PEEK composites under the dry sliding condition

Effect of coating Al2O3 reinforcing particles on the interface and mechanical properties of 6061 alloy aluminium matrix composites

Influence of the Reinforcement Phase Composition on the Structure and Abrasive Wear Resistance of Aluminum Matrix Composites Reinforced with B4C and SiC

Fretting wear behaviors of nanometer Al2O3 and SiO2 reinforced PEEK composites

Importance of Al2TiO5 particle on the mechanical and wear performance of stir cast AA6061 composite using Central Composite Design

Friction and wear characteristics of in-situ Cr+(Cr,Al)2O3 composite coating fabricated by plasma spraying

Effect of Al2O3 on Microstructure and Corrosion Characteristics of Al/Al2O3 Composite Coatings Prepared by Cold Spraying

Microstructure, Mechanical Property and Wear Performance of Cold Sprayed Al5056/SiCp Composite Coatings: Effect of Reinforcement Content

Preparation and Friction Properties of SiC-Al2O3/2A50 Co-Continuous Composites

Effects of nanoceramic particle size and content on the wear resistance of micro-arc oxidation coatings for 2A12 aluminum alloy

Microstructure and Properties of Cold-Sprayed Al- X %al 2 O 3 Composite Coatings on LA43M Mg-Li Alloy

Influence Factors on Wear Resistance of Two Alumina Matrix Composites

Improved wear and corrosion resistance of alumina alloy by MAO and PECVD

Tribological and Corrosion Behaviors of Al2o3/Polymer Nanocomposite Coatings

Tribological and Corrosion Properties of Al2O3@Y2O3-Reinforced Ni60A Composite Coatings Deposited Using Laser Cladding