Abstract:ZnO nano-arrays were successfully prepared on silicon substrates with seed film by hydrothermal inversion growth method. The seed films prepared by magnetron sputtering are generally suitable for the preparation of perfect ZnO nano-array films. The effect of solution concentration, reaction time and hydrothermal temperature on the morphology were analyzed systematically. For the ZnO nano-arrays prepared at the same temperature, the arrays cultivated in low-concentration growth solution were arranged neatly, the morphology was regular and the cross sections were hexagonal. With the concentration increasing, the nano-rods got longer and their tops became thinner. Prolonging the hydrothermal aging time helps optimize the morphology of the nano-arrays, which is very important for subsequent device preparation. Increasing hydrothermal temperature can shorten the aging time and effectively resist the environmental difference in different directions of the nano-rods, which can promote the disappearance of the upper tips and the formation of perfect nano-rod arrays. All the phenomena are determined by the growth mechanism of the ZnO nano-array. The growth mechanism was deduced in this paper according to the growing patterns reflected in experiments. The UV light emission of ZnO nano-array at 370 nm shows a certain regularity and the regularity is related to the change of morphology with solution concentration and hydrothermal temperature. This is very important for developing the application in optoelectronic devices.

Growth and comparison of different morphologic ZnO nanorod arrays by a simple aqueous solution route

Conversion of large-scale oriented ZnO rod array into nanotube array under hydrothermal etching condition via one-step synthesis approach

Effect of ammonia on morphology, wettability and photoresponse of ZnO nanorods grown by hydrothermal method

Effect of UV irradiation on the properties of ZnO nanorod arrays prepared by hydrothermal method

Alignment-controlled Hydrothermal Growth of Well-Aligned ZnO Nanorod Arrays

A Simple Route to Controllable Growth of ZnOnanorod Arrays on Conducting Substrates

ZnO Nanorod Arrays: Field-assisted Growth in Aqueous Solution and Field Emission Properties

Large-scale fabrication of tower-like, flower-like, and tube-like ZnO arrays by a simple chemical solution route

Growth of Arrayed Nanorods and Nanowires of ZnO from Aqueous Solutions

Fabrication and Morphology of ZnO Nanorods Array Prepared from Aqueous Solution under an Assisted Electrical Field

Arrays of ZnO Nanowires Fabricated by a Simple Chemical Solution Route

Facile and Controllable Growth of Zno 1d Nanostructure Arrays on Zn Substrate by Hydrothermal Process

Growth of flower-like ZnO on ZnO nanorod arrays created on zinc substrate through low-temperature hydrothermal synthesis

Preparation of ZnO Nanorod Arrays by Seed-assisted Chemical Bath Deposition Method

A Novel Low-Temperature Chemical Solution Route for Straight and Dendrite-Like Zno Nanostructures

A simple route to scalable fabrication of perfectly ordered ZnO nanorod arrays

Mechanical-Agitation-Assisted Growth of Large-Scale and Uniform ZnO Nanorod Arrays Within 3D Multichannel Monolithic Substrates

Hydrothermal Synthesis of Well-Aligned ZnO Nanorod Arrays on Silicon

Ordered Growth and Photoluminescence of ZnO Nano-Arrays on Silicon Substrates with Seed Film by Hydrothermal Method

Controllable Growth of Highly Ordered ZnO Nanorod Arrays Via Inverted Self-Assembled Monolayer Template.

Growth of Arrayed ZnO Nanowires Using a Solution Method