Effect of the Powder Size Distribution on the Hot Deformation Behavior of a Novel Nickel-based Powder Metallurgy Superalloy
Yang Jinlong,Cheng Junyi,Li Yuan,Xiong Jiangying,Long Anping,Guo Jianzheng
2022-01-01
Rare Metal Materials and Engineering
Abstract:The effects of the powder size distribution on the hot deformation behavior and the microstructural differences of a novel nickel-based powder metallurgy superalloy (WZ-A3) were studied by SEM, EDS, EBSD, OM, and the thermal simulation testing machine. The results show that compared with HIP-01 sample made from fine powder, the dendrite structure of coarse powder is obvious and the composition segregation is serious. The residual primary gamma' of the HIP-02 sample made from the coarse powder is more than that of the HIP-01 sample. At the low temperature (1050, 1080 degrees C) and high strain rates (1, 0.1 s(-1)), the peak stress of HIP-01 sample is higher than that of HIP-02 sample. After hot compression, the crack situation at the edge of HIP-01 sample is more severe than that of HIP-02 sample. Most of the original microstructure of HIP-01 sample are retained, and the crack is generated at the prior particle boundary (PPB), while some recrystallized structure appears at the edge of HIP-02 sample. At 1080 degrees C/0.001 s(-1), the peak stress of HIP-02 sample is about 30 MPa lower than that of HIP-01 sample. The recrystallization phenomenon of HIP-02 sample during hot compression is obvious and the recrystallized grains are uniform. The HIP-01 has necklace crystal structure, and the recrystallization is not sufficient. The coarse gamma' can promote the recrystallization of HIP-02 sample at 1050 and 1080 degrees C. At high temperature (1150 degrees C) and low strain rates (0.001, 0.01 s(-1)), the gamma' dissolve into. matrix, and the thermal deformation behavior of the two samples is similar. No cracks occur in the samples, and the microstructure is fully recrystallized. The abnormal grown grains are found in the both samples at 1150 degrees C/0.001 s(-1).