Abstract:Environmental barrier coatings (EBCs) are increasingly being used in the high-temperature sections of gas turbines because of their protective effects on SiC fiber-reinforced SiC ceramic matrix composites (SiCf/SiC CMCs) when subjected to high-temperature water oxygen corrosion. The objective of this study was to investigate the failure behavior of EBCs prepared on SiCf/SiC CMC matrix materials under coupled high-temperature and load conditions. A plasma spray-physical vapor deposition (PS-PVD) method was used to prepare Si/3Al2O3·2SiO2/Yb2SiO5 EBC composite coatings on the surface of SiCf/SiC ceramic matrix composites. In situ scanning electron microscopy was used to study the evolutionary behavior of the coating surface cracks at different temperatures and the failure and fracture mechanism of the coating/substrate when held at 766 °C and subjected to different loading conditions. The results show that no significant crack extension occurred on the coating surface as the temperature of the coated specimen increased from room temperature to 766 °C in the absence of an applied tensile load, indicating that the effect of a single temperature factor on the failure of the specimen was negligible. However, under coupled high-temperature and load conditions, the specimens fractured at a load of 340 N when subjected to 766 °C, indicating that the coated sample is more likely to fail when subjected to high-temperature and tensile loading. The step-like fracture exhibits features consistent with the coating fracture and spalling caused by surface cracks extending from the coating surface to the interior. The spalling, large crack formation and step-like shape of the fracture in the coating and the substrate indicate that cracks were generated between the coating and the substrate under the coupled high-temperature and load conditions. The generation and extension of cracks in both parts eventually led to full specimen rupture.

High-velocity impact damage by projectile and tension after impact behavior at 1300 °C for SiC/SiC with environment barrier coating

Experimental and numerical study on projectile impact damage of EBC-SiC/SiC

Thermal Shock Performance of CVD Tungsten Coating at Elevated Temperatures

Influence of Surface Morphology and Microstructure on Performance of CVD Tungsten Coating under Fusion Transient Thermal Loads

Thermal Shock Damage and Failure Mechanism of 2D Laminated SiC/SiC with Barium‐Strontium Aluminosilicate‐Based Environmental Barrier Coating

In Situ High-Temperature Tensile Fracture Mechanism of PS-PVD EBCs

Microstructure and Thermal Property Evolution of Plasma-Sprayed Lu2SiO5 EBCs Under High Temperature Environments

Environmental barrier coatings on SiC without a silicon bond coating: oxidation resistance, failure modes, and future improvements

Influence of post heat treatment on the high-temperature performances of multi-layered thermal/environmental barrier coatings on SiC-based composites

Properties evolution and damage mechanism of SiC/SiC composites after thermal shock at 1300 °C

Thermal shock resistance and bonding strength of tri-layer Yb2SiO5/mullite/Si coating on SiCf/SiC composites

Mechanical Properties and Damage Analysis of SiCf/SiC and SiCf/SiC-EBC Composites in High-Temperature Combustion Gas Environment

Oxidation resistance of SiCf/SiC composites with three-layer environmental barrier coatings up to 1360 °C in air atmosphere

Thermal cycling and steam corrosion behavior of Yb3Al5O12‐based multilayered environmental barrier coatings for SiCf/SiC

High-temperature mechanical properties and oxidation resistance of SiCf/SiC ceramic matrix composites with multi-layer environmental barrier coatings for turbine applications

Cyclic oxidation and water vapor corrosion behaviors of multi-layer environmental barrier coatings with HfO2-Si bond coat for SiCf/SiC

Failure mechanism of ytterbium silicate/silicon bi-layer environmental barrier coatings on SiCf/SiC composites upon long-time water vapor and oxygen corrosion test

Rear Earth Oxide Multilayer Deposited by Plasma Spray-Physical Vapor Deposition for Envisaged Application as Thermal/Environmental Barrier Coating

Oxidation resistance and thermal shock behavior of tri-layer Si/Si–Yb2SiO5/Yb2SiO5–SiC environmental barrier coatings at 1300 °C

Failure behavior of SiC/SiC with BSAS-based EBC in gas combustion environment

Oxidation behavior and interface evolution of tri-layer Si/Yb2SiO5/LaMgAl11O19 thermal and environmental barrier coatings under isothermal heat treatment at 1300 °C