Abstract:The thermal shock damage behavior of SiC/SiC‐EBC is systematically investigated. Coating cracking or even peeling occurs due to thermal stress mismatch, which acts as channels for oxygen, leading to oxidative damage of Si coatings and partial SiC/SiC substrate. However, delamination within SiC/SiC substrate is the main cause of SiC/SiC‐EBC failure. Thermal shock damage is a key issue for the stable service of SiC/SiC with environmental barrier coating (EBC) in aero‐engines. The thermal shock damage behavior of SiC/SiC with barium‐strontium aluminosilicate (BSAS)‐based EBC in an air atmosphere quenched by air and water media between RT and 1200 °C is systematically investigated. After 600 thermal shock cycles, cracks form in the EBC due to a sharp increase in the internal thermal stresses, and a SiO2 TGO layer is formed on the Si bonding coat. Based on the TGO thickness, damage within BSAS/mullite coatings is quantified by the oxygen permeability (2.541 × 10−11 mol·(atm cm s)−1), which is increased by 2.5 times compared to static oxidation. Despite cracking damage occurring in the SiC matrix of SiC/SiC substrates, the load‐bearing capability of SiC fibers is improved due to the modulus matching of the fiber/matrix. Oxidation damage is dominated the degradation of the performance of SiC/SiC substrates, whose flexural strength is decreased by 15% after 600 cycles. In the thermal shock test quenched by water media, the strength retention of SiC/SiC‐EBC is below 60%, and an increase in internal defects and even delamination of the SiC/SiC substrate are the main reasons for the thermal shock failure of SiC/SiC‐EBC.

Environmental barrier coatings on SiC without a silicon bond coating: oxidation resistance, failure modes, and future improvements

Silicon‐based bond coatings for environmental barrier coatings: Present status and prospective

Failure mechanism of ytterbium silicate/silicon bi-layer environmental barrier coatings on SiCf/SiC composites upon long-time water vapor and oxygen corrosion test

Thermal cycling and steam corrosion behavior of Yb3Al5O12‐based multilayered environmental barrier coatings for SiCf/SiC

Cyclic oxidation performances of new environmental barrier coatings of HfO2-SiO2/Yb2Si2O7 coated SiC at 1375 °C and 1475 °C in the air environment

High Temperature Corrosion of (er0.25tm0.25yb0.25lu0.25)2si2o7 Environmental Barrier Coating Material Subjected to Water Vapor and Molten Calcium–magnesium–aluminosilicate (CMAS)

Cyclic oxidation and water vapor corrosion behaviors of multi-layer environmental barrier coatings with HfO2-Si bond coat for SiCf/SiC

Corrosion behavior and failure mechanism of SiC whisker and c-AlPO4 particle-modified novel tri-layer Yb2Si2O7/mullite/SiC coating in burner rig tests

β‐Cristobalite thermal expansion and stability in environmental barrier coating systems

Thermal Shock Damage and Failure Mechanism of 2D Laminated SiC/SiC with Barium‐Strontium Aluminosilicate‐Based Environmental Barrier Coating

Investigation of Yb2SiO5/BSAS/Si coating on Cf/SiC composites: processing and steam corrosion behavior

High-temperature mechanical properties and oxidation resistance of SiCf/SiC ceramic matrix composites with multi-layer environmental barrier coatings for turbine applications

Thermal cycling behavior of bi-layer Yb2Si2O7/SiC EBC-coated Cf/SiC composites in burner rig tests

Oxidation resistance of SiCf/SiC composites with three-layer environmental barrier coatings up to 1360 °C in air atmosphere

Abradable ytterbium disilicate environmental barrier coatings: A story of CMAS and combined CMAS-erosion performance

Rear Earth Oxide Multilayer Deposited by Plasma Spray-Physical Vapor Deposition for Envisaged Application as Thermal/Environmental Barrier Coating

Corrosion behavior and mechanism of ytterbium silicates environmental barrier coatings to thermal cycling in water vapor

Oxidation properties of tri-layer ytterbium-disilicate/mullite/silicon-carbide environment barrier coatings for Cf/SiC composites

Influence of post heat treatment on the high-temperature performances of multi-layered thermal/environmental barrier coatings on SiC-based composites

Thermochemical Stability of Yb 2 Si 2 O 7 Environmental Barrier Coatings During Thermal Cycling and Water Vapor Corrosion at 1350 °C

Oxygen diffusion through environmental barrier coating materials