Effects of Ellipsoidal Corrosion Defects on Failure Pressure of Corroded Pipelines Based on Finite Element Analysis

J. Zhang,Z. Liang,C.J. Han

DOI: https://doi.org/10.1016/s1452-3981(23)06684-1

IF: 1.541

2015-06-01

International Journal of Electrochemical Science

Abstract:Failure pressures of corroded pipeline with single-point and multi-point corrosion pit were investigated by finite element method in this paper. Effects of internal pressure, length, depth and spacing of corrosion pits on failure pressure of corroded pipeline were discussed. The results show that no matter for axial corrosion pit or ring corrosion pit, the maximum stress appears on the bottom of single-point corrosion pit along pipeline axis direction, and the minimum stress appears on the end along pipeline ring direction. Von Mises stress and plastic strain increase with the increasing of internal pressure. Failure pressure of corroded pipeline decreases with the increasing of corrosion pit depth, but it increases with the increasing of wall thickness. With the increasing of corrosion pit length, failure pressure of corroded pipeline with axial corrosion pit decreases, while it increases for ring corrosion pit. Corroded pipeline with multi-point corrosion pit is more prone to failure than with single-point corrosion pit. For multi-point corrosion pit, with the increasing of internal pressure, the maximum plastic strain first appears on one end of the ellipsoidal corrosion pit and then on the bottom. Failure pressure of corroded pipeline increases gradually with the spacing increases.

electrochemistry