Abstract:Abstract For more than 30 years, Pb–Bi alloy and Wood's metal (50% Bi, 26.7% Pb, 13.3% Sn, and 10% Cd) have been used as representative superconducting solder intermedia to establish superconducting joints between NbTi and Nb 3 Sn wires in high-field nuclear magnetic resonance magnet systems. However, the use of Pb and Cd has been severely restricted by environmental regulations, such as the Restriction of Hazardous Substances Directive. Herein, a novel method of forming a superconducting joint between NbTi and Nb 3 Sn wires without Pb and Cd has been proposed. This approach is based on metallurgical bonding processes using a superconducting Nb-alloy intermedium, whose fine microstructure is maintained even after exposure to temperatures higher than 650 °C. Further, fine crystal defects become sources of magnetic flux pinning centers. Among transition elements close to Nb, Hf is considered the most suitable additive for realizing high-temperature-tolerable (HTT) superconducting Nb-alloy intermedia. Utilizing the HTT characteristic of Nb–Hf, a superconducting joint between Nb 3 Sn filaments and one end of the Nb–Hf alloy core was created by forming a superconducting Nb 3 Sn layer at the interface through a chemical reaction. The other end of the Nb–Hf alloy core was cold-pressed with NbTi filaments, to connect their active new surfaces to each other in order to create a superconducting joint. Ultimately, a superconducting joint between NbTi and Nb 3 Sn wires was realized with a high critical magnetic field ( B c 2 ) of more than 1 T. The formation of the superconducting joint was confirmed by current decay measurements. This method of forming a superconducting joint is promising for application in environmentally friendly nuclear magnetic resonance magnet systems. Graphical abstract

Superconducting Connections Between NbTi Thin Films With NbN Paste

Fabrication of Nbti Superconducting Joint by Electromagnetic Forming Method

Development of Electromagnetic Forming Nbti Superconducting Joint

Penetration depth and critical fields in superconducting NbTi thin films grown by co-sputtering at room temperature

Characterization of thin-film NbN superconductor for single-photon detection by transport measurements

Structural transitions in superconducting NbTiN thin films

Controlling the Superconducting Critical Temperature and Resistance of NbN Films through Thin Film Deposition and Annealing

Superconducting Nb interconnects for Cryo-CMOS and superconducting digital logic applications

Properties of Nb\_xTi\_{(1-x)}N thin films deposited on 300 mm silicon wafers for upscaling superconducting digital circuits

NbN Films on Flexible and Thickness Controllable Dielectric Substrates

Ultrathin Nbtin Films with High Ti Composition for Superconducting Nanowire Single Photon Detectors

2D high temperature superconductor integration in contact printed circuit boards

Substrate mediated nitridation of niobium into superconducting Nb2N thin films for phase slip study

Growth and superconductivity of niobium titanium alloy thin films on strontium titanate (001) single-crystal substrates for superconducting joints

Preparation and Superconducting Properties of Thin Films of Some Binary Transition Metal Alloy Systems

Superconducting properties of very high quality NbN thin films grown by high temperature chemical vapor deposition

Improvement of the Superconducting Properties of Nbn Thin Film on Single-Crystal Silicon Substrate by Using A Tin Buffer Layer

Pressure Tuning of Superconductivity in TiN Thin Films

Fabrication and Characterization of Superconducting Films for Superconductor-Topological Insulator Hybrid Devices

Properties of NbxTi(1-x)N thin films deposited on 300 mm silicon wafers for upscaling superconducting digital circuits.

High-temperature-tolerable superconducting Nb-alloy and its application to Pb- and Cd-free superconducting joints between NbTi and Nb3Sn wires