Fracture mode and compressive strength of ice-templated porous zirconia

Jinzhu Zou,Huiwen Xiong,Yujuan Huang,Kechao Zhou,Dou Zhang

DOI: https://doi.org/10.1016/j.ceramint.2021.03.051

IF: 5.532

2021-06-01

Ceramics International

Abstract:<p>Porous zirconia with different porosity and pore architecture were prepared by adjusting the solid loading and the binder concentration of the suspensions, and freezing rate via an ice-templating method. The transition of the fracture mode and the relationship between the compressive strength and process parameters were identified and investigated. The load-displacement curves showed a variation from a buckling fracture at porosity above 70 % to a brittle fracture in the porosity range from 35.3 % to 55.5 %, owning to the increased resistance of the ceramic walls to buckling. As the porosity decreased from 75.0 % to 35.3 %, the mean compressive strength of the samples increased from 4.5 MPa to 197.1 MPa. Under buckling fracture, increasing the binder concentration from 2 wt% to 4 wt% contributed to the improvement of the mean compressive strength from 5.5 MPa to 14.8 MPa, although samples had similar porosity level (~73 %). For brittle fracture, samples with porosity around 54 % exhibited the improvement of mean compressive strength from 45.5 MPa to 75.1 MPa when increasing the freeze velocity from 8 °C/min to 25 °C/min.</p>

materials science, ceramics