Microstructural characteristics and fracture mechanism of in situ pressureless-sintered MgAlON–MgO ceramic from spent MgO–C brick

Xiang Cheng,Xiwang Miao,Lei Liu,Ying Zhang,Min Guo,Fangqin Cheng,Mei Zhang

DOI: https://doi.org/10.1016/j.matchar.2021.111391

IF: 4.537

2021-09-01

Materials Characterization

Abstract:MgAlON–MgO ceramic was synthesised in situ at 1600 °C from spent MgO–C brick by pressureless sintering. Microstructural characteristics of the MgAlON–MgO ceramic were analysed using scanning electron microscopy and transmission electron microscopy, indicating that MgAlON is a continuous phase in the ceramic. Impurity phases introduced from spent MgO–C bricks in the MgAlON–MgO ceramic exist in the form of CaMgSiO4 and MgFe2O4. The CaMgSiO4 phase is combined directly with MgO, whereas MgFe2O4 is embedded in MgO. Furthermore, the effect of the spent MgO–C brick on the flexural strength of MgAlON–MgO ceramic was studied by adjusting the added quantity of spent brick, indicating that flexural strength decreases from 172 MPa to 46 MPa as spent brick addition increases from 11.1 wt% to 52.9 wt%, which was attributed to the synergistic effect of the MgO content in MgAlON–MgO and the C content from the spent brick. Moreover, the CaMgSiO4 impurity increases the density of the MgAlON–MgO ceramic and subsequently enhances its flexural strength, whereas MgFe2O4 has no obvious effect on properties of the ceramic.

materials science, multidisciplinary,metallurgy & metallurgical engineering, characterization & testing