Effect of Zn deficiency on the enhancement of yellowish green persistent phosphor Dy3+-activated SrZn2(PO4)2

Yichao Sun,Wen Chen,Siyuan Liu,Songhe Yan,Siwei Zhang,Lingfeng Huang,Zishan Zheng

DOI: https://doi.org/10.1016/j.solidstatesciences.2021.106754

IF: 3.752

2021-11-01

Solid State Sciences

Abstract:The yellowish green long persistent phosphors SrZn2-δ-x(PO4-0.5δ)2:xDy3+ were prepared using high temperature solid state method with decay time of about 6 h. The material shows the strongest yellow emission peak at 572 nm attributed to the 4F9/2 → 4H13/2 transition of Dy3+, as well as the second strongest blue one at 482 nm which is contributed by the transitions 4F9/2 → 4H15/2 of Dy3+ and the Zn defects. The compounds of XPS, TL, and EPR spectra as well as the defect equation were used to analyze various defects in the materials. Dy3+ ions are acted as both emission centers and defect suppliers, and Zn deficiency is beneficial to the improvement of luminescence properties of SrZn2-δ-x(PO4-0.5δ)2: xDy3+. Based on the energy band theory and the crystal defect theory, the luminescence mechanism of materials was explored.

chemistry, physical, inorganic & nuclear,physics, condensed matter