Tuning Emission Color and Improving the Warm-White Persistent Luminescence of Phosphor BaLu2Al2Ga2SiO12:Pr3+via Zn2+ Co-Doping.
Weihong Yuan,Ran Pang,Tao Tan,Haiyan Wu,Shangwei Wang,Jiangyue Su,Jiutian Wang,Shengjian Jiao,Chengyu Li,Hongjie Zhang
DOI: https://doi.org/10.1039/d1dt01913a
IF: 4
2021-01-01
Dalton Transactions
Abstract:In this article, we synthesized a series of new warm-white emitting persistent luminescent phosphors by co-doping Zn2+ into Pr3+ activated BaLu2Al2Ga2SiO12, and systematically investigated the effect of Zn2+ co-doping on both their photoluminescence and persistent luminescence properties. Following the removal of UV excitation, the phosphor emits warm-white persistent luminescence consisting of greenish-blue and red emissions originating from 3P0 and 1D2 multiplet electron transitions at the 4f level of Pr3+. The luminescence properties of the Ba1-xZnxLu2Al2Ga2SiO12:Pr3+ phosphors can be modified by changing the content of Ba/Zn in the host, which affects the non-radiative energy flow between 5d1-3P0-1D2 levels and resultantly enhances the intensity of the 4f → 4f transition. Compared with the undoped sample, Zn2+ co-doping can significantly enhance the persistent luminescence intensity of the phosphors in the range of 400-800 nm and reduce the intensity in the UV region. Meanwhile, Zn2+ co-doping can also change the intensity ratio between the greenish-blue and red emissions, and the persistent luminescence color can be tuned from red to warm-white with the increase of Zn2+ concentration. Besides, the Zn2+ ions entering the crystal lattice also enhance the persistent luminescence performance by modifying the defect levels in the phosphor. For the optimized phosphor, bright warm-white persistent luminescence can be observed by the naked eye in the dark after the removal of the excitation source for 4 h. Based on the experimental results, a feasible mechanism was also proposed to reveal the persistent luminescence generation process for the BaLu2Al2Ga2SiO12:Pr3+,Zn2+ phosphor.