Synthesis Of New Yellow-Emitting Phosphors Gd2o3: Dy3+ By The Hydrothermal Method And Luminescent Properties

Zhai Yongqing,Liu Yahong,Li Lanfen,Qiu Liying,Jiang Nan

2012-01-01

Rare Metal Materials and Engineering

Abstract:New yellow-emitting phosphors Gd2O3:Dy3+ were prepared by the hydrothermal method using urea as the precipitation agent. FT-IR, XRD, SEM and Fluorescence spectrophotometer were used to analyze and characterize the hydrothermal precursor and the target product. The results show that the precursor is Gd-2(CO3)(3)center dot xH(2)O. Gd2O3:Dy3+ with pure cubic phase can be obtained after the precursor was calcined at 900 degrees C. The microstructure of the sample needle in shape with a length about 10-200 mu m. The excitation spectrum is composed of a series of peaks located at 239, 279, 314 and 353 nm respectively, and the strongest peak is at 279 nm. The emission spectrum mainly consists of two parts, the blue emitting peaks (band) in the range of 460-500 nm and the yellow-green emitting peaks (band) in the range of 560-590 nm. The strongest emission peak is at 573 nm, which is ascribed to the transition of F-4(9/2)-H-6(13/2) of Dy3+. The doped-Dy3+ concentration has agreat effect on the fluorescence intensity of Gd2O3:Dy3+. The fluorescence intensity increases with the doped-Dy3+ concentration, and then decreases. The strongest fluorescence intensity can be obtained when the doping concentration is 0.8%. The concentration quenching is mainly caused by the interaction of dipole-dipole.