Warm-white luminescence of Dy3+ and Sm3+ co-doped NaSrPO4 phosphors through energy transfer between rare earth ions

Wen Yan,Junhan Li,Wentao Zhang,Xi Gao,Peicong Zhang

DOI: https://doi.org/10.1007/s10854-021-06219-4

2021-05-28

Abstract:Series of white light-emitting NaSrPO₄:Dy³⁺ phosphors were synthesized via a sol–gel method. Small amounts of Sm³⁺ ions were co-doped into the phosphors to enhance their luminescence. The effects of Dy³⁺/Sm³⁺ co-doping concentrations and synthesis temperature on the phosphors' structures and luminescence properties were investigated. The results of X-ray diffraction confirmed that the characteristic diffraction peaks of the phosphors were in accord with those of the standard NaSrPO₄ structure. Energy dispersive spectroscopy indicated that the NaSrPO₄:Dy³⁺ samples were prepared with stoichiometric ratios of elements. Under ultraviolet light excitation of 348 nm, the NaSrPO₄:Dy³⁺ phosphors emitted a white light which was composed of two emission peaks at 484 nm (blue) and 577 nm (yellow) corresponding to the magnetic dipole transition ⁴F_9/2 → ⁶H_15/2 and electronic dipole transition ⁴F_9/2 → ⁶H_13/2 of Dy³⁺ ions, respectively. Based on Sm³⁺ co-doping, a characteristic red emission at 602 nm arose and a warm-white light containing a lower <i>CCT</i> value was obtained. Besides, the luminescence lifetime of Dy³⁺ decreased while that of Sm³⁺ increased as dosages of Sm³⁺ were added, indicating efficient energy transfer from Dy³⁺ to Sm³⁺ happened. Therefore, NaSrPO₄:Dy³⁺, Sm³⁺ phosphors are promising candidates for application in warm-white light-emitting diodes.

engineering, electrical & electronic,materials science, multidisciplinary,physics, condensed matter, applied