Abstract:The interface bonding strength between adjacent melt lines formed in the melt-extrusion-based 3D printing (ME3DP) process largely governs the mechanical properties of the as-printed parts. But this normally leads to mechanical anisotropy of which the mechanism is not very clear. In this work, based on the investigation of the temperature attenuation behavior of newly deposited thermoplastic polyurethane (TPU) melt in a ME3DP process, the mechanical dependence on the interface development was explored. First, the temperature attenuation of a newly deposited melt in an open environment was found to be well fitted by the Power-law function. Then the effect of envelope temperature on the tensile property of the as-printed TPU was studied using an electric-heating bed (EHB) which endowed the whole printed sheets with a temperature near EHB temperature. To explore the mechanism of mechanical anisotropy, tensile testing was then performed for the printed sheets in both longitudinal and transverse directions, respectively. Results showed that the ultimate tensile strength (UTS), as well as the elongation at break measured along the transverse direction, increased with the increase of EHB temperature, which was mainly attributed to the improved interface bonding. In comparison, the UTS along the longitudinal direction kept relatively stable, slightly increasing initially and then followed by a minor decrease. Of note is the fact that the mechanical properties of printed parts were governed simultaneously by both the wall-shear-induced orientation effect of molecular chains at the surface of the deposited melt line and the crystallization morphology inside the deposited molten filament was concluded in this work. A high envelope temperature not only promoted the molecular diffusion around the interface layer, enhanced the interface bonding, and overcome the mechanical anisotropy but also promoted the crystallization kinetics. The printed TPU with developed crystallized morphology exhibited improved yield stress in the longitudinal direction above a critical temperature. This work demonstrates an insight into the mechanical anisotropy of 3D-printed polymers, paving the way to print high-strength parts via ME3DP.

Desktop printing of 3D thermoplastic polyurethane parts with enhanced mechanical performance using filaments with varying stiffness

3D Printable Elastomers with Exceptional Strength and Toughness

Experimental analysis of the tensile property of FFF-printed elastomers

Interfacial Bonding During Multi-Material Fused Deposition Modeling (FDM) Process Due to Inter-Molecular Diffusion

Study on Efficient Fused Deposition Modelling of Thermoplastic Polyurethane Inflatable Wall Features for Airtightness

Mathematical and Statistical Analysis of Fused Filament Fabrication Parameters for Thermoplastic Polyurethane Parts via Response Surface Methodology

Influence of 3D Printing Parameters on the Interlayer Bonding Strength for TPU Soft Materials

Optimizing 3D Printing Process Parameters for the Tensile Strength of Thermoplastic Polyurethane Plastic

An insight into the tensile anisotropy of 3D-printed thermoplastic polyurethane

Fabrication of Flexible Wood Flour/thermoplastic Polyurethane Elastomer Composites Using Fused Deposition Molding

Improving Tensile Properties of Polylactic Acid Parts by Adjusting Printing Parameters of Open Source 3D Printers

A Comparative Analysis of Chemical, Plasma and In Situ Modification of Graphene Nanoplateletes for Improved Performance of Fused Filament Fabricated Thermoplastic Polyurethane Composites Parts

A comparative evaluation of compression moulded and fused deposition modelling 3D printed thermoplastic polyurethane

Preparation of polycarbonate/poly(lactic acid) with improved printability and processability for fused deposition modeling

Study of the adhesion between TPU and PLA in multi-material 3D printing

Development of isotactic polypropylene‐based 3D printing materials with good dimensional accuracy and excellent impact properties

Parametric Optimization of 3D Printing Process Hybridized with Laser-Polished PETG Polymer

Mechanical dependence of 3D-printed thermoplastic polyurethane reinforced with minor continuous carbon fibres

On the 3D printing of polypropylene and post-processing optimization of thermomechanical properties

Effect of 3D Printing Process Parameters on Mechanical Properties of TPU Samples