Abstract:The interface bonding strength between adjacent melt lines formed in the melt-extrusion-based 3D printing (ME3DP) process largely governs the mechanical properties of the as-printed parts. But this normally leads to mechanical anisotropy of which the mechanism is not very clear. In this work, based on the investigation of the temperature attenuation behavior of newly deposited thermoplastic polyurethane (TPU) melt in a ME3DP process, the mechanical dependence on the interface development was explored. First, the temperature attenuation of a newly deposited melt in an open environment was found to be well fitted by the Power-law function. Then the effect of envelope temperature on the tensile property of the as-printed TPU was studied using an electric-heating bed (EHB) which endowed the whole printed sheets with a temperature near EHB temperature. To explore the mechanism of mechanical anisotropy, tensile testing was then performed for the printed sheets in both longitudinal and transverse directions, respectively. Results showed that the ultimate tensile strength (UTS), as well as the elongation at break measured along the transverse direction, increased with the increase of EHB temperature, which was mainly attributed to the improved interface bonding. In comparison, the UTS along the longitudinal direction kept relatively stable, slightly increasing initially and then followed by a minor decrease. Of note is the fact that the mechanical properties of printed parts were governed simultaneously by both the wall-shear-induced orientation effect of molecular chains at the surface of the deposited melt line and the crystallization morphology inside the deposited molten filament was concluded in this work. A high envelope temperature not only promoted the molecular diffusion around the interface layer, enhanced the interface bonding, and overcome the mechanical anisotropy but also promoted the crystallization kinetics. The printed TPU with developed crystallized morphology exhibited improved yield stress in the longitudinal direction above a critical temperature. This work demonstrates an insight into the mechanical anisotropy of 3D-printed polymers, paving the way to print high-strength parts via ME3DP.

Tensile properties of 3D printed structures of polylactide with thermoplastic polyurethane

Single-layer Temperature-Adjusting Transition Method to Improve the Bond Strength of 3D-Printed PCL/PLA Parts

The Influence of 3D Printing Parameters on Adhesion between Polylactic Acid (PLA) and Thermoplastic Polyurethane (TPU)

Study of the adhesion between TPU and PLA in multi-material 3D printing

3D printing of PLA-TPU with different component ratios: fracture toughness, mechanical properties, and morphology

Mechanical properties of the FFF sandwich-structured parts made of PLA/TPU multi-material

Interfacial Bonding During Multi-Material Fused Deposition Modeling (FDM) Process Due to Inter-Molecular Diffusion

Enhancing interlaminar adhesion in multi-material 3D printing: A study of conductive PLA and TPU interfaces through fused filament fabrication

An insight into the tensile anisotropy of 3D-printed thermoplastic polyurethane

A comparative evaluation of compression moulded and fused deposition modelling 3D printed thermoplastic polyurethane

Study on performance characteristics of fused deposition modeling 3D ‐printed composites by blending and lamination

Mechanical Characteristics of Thermoplastic Polymers for 3d Printed Hybrid Structures

Mechanical properties of 3D printed polylactic acid elements: Experimental and numerical insights

Mechanical dependence of 3D-printed thermoplastic polyurethane reinforced with minor continuous carbon fibres

Comprehensive characterization of mechanical and physical properties of PLA structures printed by FFF-3D-printing process in different directions

3D printing thermo-responsive shape memory polymer composite based on PCL/TPU blends

Post-processing in multi-material 3D printing

Tensile failure strength and separation angle of FDM 3D printing PLA material: Experimental and theoretical analyses

Compression Performance with Different Build Orientation of Fused Filament Fabrication Polylactic Acid, Acrylonitrile Butadiene Styrene, and Polyether Ether Ketone

On Laminated Object Manufactured FDM-Printed ABS/TPU Multimaterial Specimens: An Insight into Mechanical and Morphological Characteristics

Effect of Printing Parameters on the Thermal and Mechanical Properties of 3D-Printed PLA and PETG, Using Fused Deposition Modeling