Abstract:Cu matrix composites have received increased attention in a wide industrial area because of their excellent mechanical properties and good electrical and thermal conductivity. However, the addition of general ceramic reinforcements often leads to a marked reduction in electrical conductivity for Cu matrix composites. In this study, the ZrB 2 -reinforced Cu composites have been developed to overcome this drawback since these metal borides possess relatively high electrical conductivity. The 5 wt.% ZrB 2 /Cu composites were prepared using hot-pressed sintering techniques at varying temperatures from 760 to 920°C. The influence of sintering temperature on the microstructure, relative density, and mechanical and electrical properties was examined. The results of the SEM observation show that ZrB 2 particles are seamlessly integrated into the Cu matrix for all ZrB 2 /Cu composites. The average grain size of the Cu matrix increases from 360 to 980 nm with the increase of the sintering temperature. The increase in sintering temperature also leads to the surface porosity decrease from 1.4 to 0.4%. The relative density and electric conductivity of the composites increase at the same time as the sintering temperature increases. However, microhardness increases and decreases, with a maximum value of 92 HV0.2 achieved at 840°C. The elastic modulus and nanohardness maps determined from the nanoindentation indicate that the reinforced ZrB 2 particles demonstrate the highest values for elastic modulus (340–500 GPa) and nanohardness (30–48 GPa). At the same time, the Cu matrix possesses a modulus of 100–200 GPa and nanohardness of about 10 GPa. TEM observation confirmed that the sintering temperature exhibits little influence on the interface reaction between ZrB 2 and Cu. Both sharp interface and interface with amorphous transition layer are observed. The variation of microhardness is mainly due to the strengthening of grain refinement and to the mismatch of the thermal expansion coefficients. The above results can provide further insights into the deeper understanding of the role of sintering temperature during hot-pressed sintering.

Microstructure and properties of dual-scale particulate reinforced copper matrix composites with superior comprehensive properties

Microstructure and Properties of In-Situ TiC Reinforced Copper Nanocomposites Fabricated Via Long-Term Ball Milling and Hot Pressing

A nano-micro dual-scale particulate-reinforced copper matrix composite with high strength, high electrical conductivity and superior wear resistance

Microstructural evolution and mechanical property of Cu‐Cr‐Zr‐ZrB2 composites subjected to cryorolling and aging treatment

A research on the electrical sliding behavior wear of dual-scale particulate reinforced copper matrix composites

Microstructural Characteristics, Electrical Conductivity and Mechanical Properties of Cu Matrix Composites Reinforced with Dual-Phase Borides

Microstructure, mechanical and tribological properties of Cu-Sn/Cr3C2/Gr composites

Influence of particulate B4C with high weight fraction on microstructure and mechanical behavior of an Al-based metal matrix composite

Realizing the combination of high strength and good ductility of Cu matrix composites with CrCoNi reinforcement particles and microlaminated structure

Mechanical, Corrosion and Wear Characteristics of Cu-Based Composites Reinforced with Zirconium Diboride Consolidated by SPS

Mechanical and tribological properties of WC particles reinforced Cu-20Zn matrix composites

Microstructure and mechanical properties of nano-carbon reinforced Mo–Cu–Zr composites

Effect of alloying element Zr on microstructure and properties of Cu−Y2O3 composites

Microstructure, properties and strengthening mechanism of Cu-TiB2-Al2O3 composite prepared by liquid phase in-situ reaction casting

Effect of Sintering Temperature on the Microstructure and Properties of High-Strength and Highly Conductive 5 wt.% ZrB2/Cu Composite

Mechanical Properties of Cu50Zr50 Amorphous/b2-Cuzr Crystalline Composites Studied by Molecular Dynamic Method

Microstructure and Wear Resistance of Cu/nano-SiC Composite

Strengthening and toughening of Cu matrix composites reinforced by metallic glass particles with variable size

Enhanced Mechanical and Electrical Properties of CuCrZr-WC Alloy Prepared by Mechanical Alloying and Spark Plasma Sintering

Abrasive Wear and Physical Properties of In-Situ Nano-TiCx Reinforced Cu–Cr–Zr Composites