Dimension effect of Y2O3 nanomaterial on microstructure and tensile properties of laser metal deposited stainless steel coatings

Xiao-yu Liu,Yi Sui,Jin-bao Li,Jun-yu Yue,Xiao-hua Sun,Li-feng Yang,Chang-sheng Liu

DOI: https://doi.org/10.1016/j.surfcoat.2021.127259

IF: 4.865

2021-08-01

Surface and Coatings Technology

Abstract:Yttrium (Y) is an engineering material used in refinement, and the physical properties of Y2O3 nanomaterials play key roles in thermal-effect of refinement. In this study, the experimental thermal-efficiencies induced by dimension of Y2O3 nanomaterials and their influence on microstructures and tensile performances of graded stainless steel coatings were investigated. To this end, 16Cr2NiSiMo stainless steel coatings were fabricated by laser metal deposition (LMD) technology in the presence of small amounts (<1 wt%) of Y2O3 nanoparticles (diameter 30–50 nm) and Y2O3 nanosheets (thickness 20–30 nm) without additional heat-treatment. Compared to Y2O3 nanosheets-modified coatings, more decline in the interlayer heat-affected zone, dendritic solidification microstructure, pore, microcrack, and taenite phase were all observed for coatings prepared in the presence of Y2O3 nanoparticles. The reason for this difference had to do with the dimension of Y2O3 nanomaterial, which directly influenced the dissociation of Y3+ ions in dendrites by decreasing the melting point of the material and transition temperature of the metastable eutectic. As a result, Y2O3 nanoparticles promoted the hardness and tensile properties of the coatings, while Y2O3 nanosheets increased microcracks and pores but declined the tensile properties. The ultimate tensile strength and elongation of the sample prepared by adding 0.75 wt% Y2O3 nanoparticles enhanced by 17% and 47.9%, respectively.

physics, applied,materials science, coatings & films

What problem does this paper attempt to address?

The paper mainly explores the effects of different morphologies of yttrium oxide (Y2O3) nanomaterials (nanoparticles and nanosheets) on the microstructure and tensile properties of stainless steel coatings prepared by Laser Metal Deposition (LMD).

Specifically, the study investigates the size effect of Y2O3 nanomaterials by adding different amounts (<1 wt%) of Y2O3 nanoparticles or nanosheets to stainless steel powder and using LMD technology to manufacture the coatings. The main findings are as follows:

1. **Role of Yttrium Oxide Nanoparticles**:
- Reduced the width of the interlayer heat-affected zone (ILHAZ) (approximately 25-30 micrometers), improving the dendritic solidification structure;
- Promoted the increase in hardness and tensile properties;
- With 0.75 wt% Y2O3 nanoparticle addition, the ultimate tensile strength and elongation of the coating increased by 17% and 47.9%, respectively.

2. **Role of Yttrium Oxide Nanosheets**:
- Increased microcracks and porosity, leading to a decrease in tensile properties;
- The reduction effect on ILHAZ width was not significant in the nanosheet form, and more needle-like phases (taenite) were generated.

3. **Mechanism Analysis**:
- Y3+ ions lowered the melting point of the alloy system, promoting dendrite refinement, thereby improving the uniformity and mechanical properties of the coating;
- Smaller Y2O3 nanoparticles could decompose more effectively, producing sufficient Y3+ ions to influence the dendrite melting point, thus optimizing the microstructure;
- In contrast, larger Y2O3 nanosheets could not fully decompose during rapid heating, thus having a smaller effect on the dendrite melting point and easily forming brittle phases.

In summary, this study aims to explore methods to optimize the microstructure and tensile properties of stainless steel coatings prepared by laser metal deposition by controlling the size of Y2O3 nanomaterials. Among them, Y2O3 nanoparticles showed better effects, while Y2O3 nanosheets might lead to a decline in coating performance.