Microstructure and properties of Mo-Si-B-Y 2 O 3 composite coating on nickel-based alloy by laser cladding

Zican Ding,Ziyu Fang,Guangyuang Wang,Chengcheng Wu,Sen Yang

DOI: https://doi.org/10.1016/j.optlastec.2023.109473

2023-04-12

Abstract:A Mo-12Si-8.5B-Y 2 O 3 composite coating was prepared on the surface of nickel-based alloy by laser cladding. In this study, the effect of Y 2 O 3 on the coating structure and properties is examined. Macroscopic morphology, microstructure, and phase structure of the coatings were examined by optical microscopy (OM), scanning electron microscopy (SEM), energy spectrometry (EDS), and X-ray diffraction (XRD). The wear resistance and high-temperature oxidation resistance of the coatings were evaluated using a high-temperature tribometer and a simultaneous thermal analyzer. The experimental results indicate that the microhardness and high-temperature oxidation resistance of the coating increased with an increase in Y 2 O 3 content. However, excessive Y 2 O 3 contributed to an increased cracking tendency of the coating and a decrease in high-temperature frictional wear resistance. The composite coating containing 1 wt.% Y 2 O 3 was of the best quality. The corresponding clad layer contained a mixture of α-Mo + Mo 5 SiB 2 (T2) + Mo 3 Si phases with a microhardness value of 931 HV 0.5 , which was 5.6 times the substrate value. The Y 2 O 3 -modified coating reached a stable state after extended oxidation at 900 °C with less mass loss. The composite coating improved the high-temperature oxidation resistance of the substrate.

optics,physics, applied