Abstract:Laser cladding technology is an effective surface modification technique. In order to prepare coating with excellent properties on the surface of the cold heading die punch, stellite-6 cladding coating with different proportions of Y2O3 was prepared on the surface of W6Mo5Cr4V2 high-speed steel using laser cladding technology in this paper. The effects of different Y2O3 contents on the macroscopic morphology, microstructure, phase analysis, microhardness, and tribological properties of the stellite-6 coatings were investigated. It was determined that the optimal Y2O3 content for the stellite-6 powder was 2%. The results showed that the coating with 2%Y2O3 had the least number of pores and cracks and exhibited good surface flatness when joined. The microstructure became finer and denser, composed mainly of branch, cellular, equiaxed, and columnar grains. The coating consisted mainly of γ-Co, Fe-Cr, and Co3Fe7 strengthening phases, indicating good metallurgical bonding between the coating and the substrate. The average microhardness reached 539 HV when 2%Y2O3 was added, a 15.2% increase compared with the unmodified multilayer coating. The friction coefficient of the clad layer was 0.356, a 21.8% improvement over the unmodified stellite-6 coating. The average worn area of the cross-section was 3398.35 μm2, a reduction of approximately 27.8% compared with the unmodified stellite-6 clad layer. The wear surface primarily exhibited abrasive wear, with fewer cavities and a smoother surface.
What problem does this paper attempt to address?
The paper primarily explores the preparation of Stellite-6 alloy coatings with different yttrium (Y2O3) contents on the surface of high-speed steel (W6Mo5Cr4V2) using laser cladding technology, and investigates the effects of Y2O3 content on the coating's macroscopic morphology, microstructure, phase composition, microhardness, and friction and wear properties.
### Research Background and Objectives
- **Background**: During operation, cold stamping dies are subjected to friction and impact under alternating loads, leading to local spalling and brittle cracking of the dies. The heat generated by continuous operation also reduces the material hardness. Laser cladding technology, as an advanced material surface treatment technology, can effectively improve these issues.
- **Objective**: By adding different proportions of Y2O3 to Stellite-6 alloy powder, the goal is to prepare coatings with excellent performance using laser cladding technology to enhance the wear resistance and corrosion resistance of the material.
### Main Research Content
- **Experimental Materials**: W6Mo5Cr4V2 high-speed steel was used as the substrate, with dimensions of 100 mm×60 mm×10 mm; Stellite-6 self-fluxing alloy powder with a particle size range of 44~149 μm; and yttrium oxide (Y2O3) powder with a particle size range of 30~100 μm.
- **Experimental Methods**:
- Prepared Stellite-6 composite coatings with different proportions of Y2O3 (2%, 3%, 4%).
- Used 6 kW laser cladding equipment with a laser power of 1600 W, a scanning speed of 15 mm/s, a powder feeding rate of 15 r/min, a laser spot diameter of 3 mm, an overlap rate of 30%, and argon as the shielding gas (5 L/min).
- Adopted synchronous laser cladding to observe the macroscopic morphology, microstructure, and phase composition of the coatings, and conducted microhardness tests and friction and wear experiments.
### Key Findings
- **Macroscopic Morphology**: When the Y2O3 content was 2%, the coating surface was relatively smooth with the least porosity and cracks.
- **Microstructure**: With 2% Y2O3 content, the grains in the coating were the finest and densest, consisting of dendrites, cellular crystals, equiaxed crystals, and columnar crystals.
- **Phase Composition**: The coating was mainly composed of γ-Co, Fe-Cr, and Co3Fe7 strengthening phases.
- **Microhardness**: After adding 2% Y2O3, the average microhardness reached 539 HV, an increase of 15.2% compared to the unmodified multilayer coating.
- **Friction and Wear Properties**: The friction coefficient of the coating with 2% Y2O3 was 0.356, an improvement of 21.8% compared to the unmodified Stellite-6 coating; the average cross-sectional wear area was 3398.35 μm2, a reduction of about 27.8%.
In summary, this study significantly improved the comprehensive performance of Stellite-6 coatings by optimizing the proportion of Y2O3 addition, achieving notable results especially in terms of microhardness and friction and wear properties.