Abstract:The infrared radiation heating textiles have attracted increasing attention aiming to address the warmth retention issue in cold weather. It still remains challenging to develop high-efficiency heating products with fast heating rate and stable heat generation. Here, a highly flexible, efficient, and wearable infrared radiation heating carbon fabric (CF) was rationally constructed using textile forming technique. Inspired by the biomimetic adhesion, the carbon fabric was chemically modified by dopamine to improve the interfacial activity on the fiber surface. Infrared radiation materials including tourmaline, ZrO2, and medical stone nanoparticles (NPs) were successfully introduced into the carbon fabric through interfacial adhesion. The permanent spontaneous polarization of both CF matrix and infrared radiation NPs can induce an enhanced current in the heater by creating an additional electrical field, benefiting to produce a fast electrothermal response and favorable heat preservation. It was found that 30% @CF, 9% ZrO2@, and 15% medical @CF exhibited excellent heat generation performance among different samples with different ingredients. The temperature can be rapidly raised up from room temperature to 58.3℃, 60℃, 59.5℃ respectively for these three samples in 10 min under a voltage of 10 V. More importantly, the composite CF is highly shape adaptive and can be fully integrated into a neck guard or industrial carpet for real application. It is expected that this infrared radiation heating CF can be widely applied in the fields of personal warmth, physical therapy, biomedical treatment, and wearable flexible electronics.

High structural stability of colored carbon fiber cloths modified by FeOOH

Chemical Treatment of Carbon Fibers and the Development of Functional Paper

Constructing Carbon-Coated Fe3O4 Hierarchical Microstructures with a Porous Structure and Their Excellent Cr(VI) Ion Removal Properties

Full-Color Tunable and Highly Fire-Retardant Colored Carbon Fibers

The Fabrication of Full Chromatography SiO2@PDA Photonic Crystal Structural Colored Fabric with High Thermal Stability

Hydroxypropyl Cellulose-Based Meter-Long Structurally Colored Fibers for Advanced Fabrics

Preparation of carbon fiber substrates with structural colors based on photonic crystals

Structural Color Fibers Directly Drawn from Colloidal Suspensions with Controllable Optical Properties

Effect of Heating Rate on Morphology and Structure of Cofe2o4 Nanofibers

Structural Colored Fabric Based on Monodisperse Cu2O Microspheres

Rapid fabrication of photonic crystal patterns with iridescent structural colors on textiles by spray coating

Structural Colored Aramid Fabric Construction and Its Application as Recyclable Photonic Catalysis

Solvothermal synthesis of microporous, crystalline covalent organic framework nanofibers and their colorimetric nanohybrid structures.

A novel Fe-containing carbon foam with hierarchical porous structure for efficient removal of organic dyes

Fiber-shaped dynamic thermal radiation-regulated device based on carbon fiber and polyaniline

Preparation of robust structural color film on cotton fabrics by caffeic acid

Effect of calcination temperatures on HfO2 fibers via electrospinning

Multicolored structural coloration of carbon nanotube fibers

Enhancing Carbon Fiber Fabrics with ALD AlxOy Coatings: An Investigation of Thickness Effects on Weight, Morphology, Coloration, and Thermal Properties

Robust and Durable Photonic Crystal with Liquid-Repellent Property for Self-Cleaning Coatings and Structural Colored Textiles

Highly flexible, efficient, and wearable infrared radiation heating carbon fabric