Abstract:Carbon fibers (CFs) have been widely used as reinforcing materials because of their excellent specific strength, specific modulus, corrosion resistance, energy absorption, and other properties. To improve the mechanical properties of CF-reinforced composites, one of the effective methods is to improve the interfacial force between the CF and the polymer through modification of CFs. The aim of this study is to modify the surface of the CF with an environmentally friendly and efficient way and to design a continuous production equipment. In this research, a continuous electro-polymerization equipment was designed, and the surface of the CFs was modified by epoxy or vinyl ether, which was initiated by photoinitiator UVI-6974 without adding any solvent and extra electrolytes. By changing the structure of monomers, polymerization time, voltage, concentration of the initiator, and the distance between CFs and electrodes, the performance and thickness of the polymer layer on the CFs were controllable. The results of scanning electron microscopy and infrared spectroscopy proved that the surface of the CFs was covered by polymers, and some unreacted functional groups remained. The mechanical performances of CF composites prepared from the BDE/DVE-3-modified CFs showed that the interlaminar shear strength improved by 46.98 and 62.02%, and the tensile strength improved by 11.40 and 16.62%, respectively, compared with unmodified CFs. This proved that the interface force between the resin and the CF was greatly improved by the thin polymer layer on the surface of the CF and the unreacted functional groups. On the other hand, if pigments or dyes were added to the polymerization system, colored CFs could be fabricated by this equipment continuously. Because of the solvent-free, low-voltage, and continuous fabrication, this electro-polymerization method has a good industrial prospect.This article has not yet been cited by other publications.

Full-Color Tunable and Highly Fire-Retardant Colored Carbon Fibers

Superdurable and fire-retardant structural coloration of carbon nanotubes

Color construction of multi-colored carbon fibers using glucose

Fiber with Butterfly Wings: Creating Colored Carbon Fibers with Increased Strength, Adhesion, and Reversible Malleability

Multicolored structural coloration of carbon nanotube fibers

High structural stability of colored carbon fiber cloths modified by FeOOH

Preparation of carbon fiber substrates with structural colors based on photonic crystals

Rapid and Scalable Synthesis of Novel Carboxylated Aramid Nanofibers for Simultaneously Improving the Strength and Toughness of Carbon Fiber/epoxy Laminates

Pearl‐Inspired Colored Carbon Fibers with Electromagnetic Interference and Optical Camouflage Properties

Hydroxypropyl Cellulose-Based Meter-Long Structurally Colored Fibers for Advanced Fabrics

The carbon fiber/epoxy composites toughened by fire-resistant glass fiber veils: Flammability and mechanical performance

Carbon Fibers Decorated by Polyelectrolyte Complexes Toward Their Epoxy Resin Composites with High Fire Safety

Scalable Structural Coloration of Carbon Nanotube Fibers via a Facile Silica Photonic Crystal Self-Assembly Strategy

Carbon-Based Fibers: Fabrication, Characterization and Application

Realizing Flexible Multicolored Electrochromism on Carbon Nanotubes through Thin-Film Interference

Multicolor, Fluorescent Supercapacitor Fiber

Advanced Functional Carbon Nanotube Fibers from Preparation to Application

A Novel Continuous Carbon Nanotube Fiber/carbon Composite by Electrified Preform Heating Chemical Vapor Infiltration

A flame retardant fabric nanocoating based on nanocarbon black particles@polymer composite and its fire-alarm application

Surface Modification of Carbon Fiber by Electro-Polymerization: Continuous Production, Thickness Control, Colorization, and Preparation of CFRP

Single Carbon Fibers with a Macroscopic-Thickness, 3D Highly Porous Carbon Nanotube Coating