Enhancing high-temperature performance of Inconel 718 LDED samples through hybrid laser polishing post-treatment

Zifa Xu,Liangjie Xu,Lizhi Su,Wentai Ouyang,Shengyuan Sun,Wei Cheng,Wei Guo,Xinqiang Ma,Wenwu Zhang,Junke Jiao

DOI: https://doi.org/10.1080/17452759.2024.2345391

IF: 10.6

2024-05-26

Virtual and Physical Prototyping

Abstract:A hybrid laser polishing post-treatment was introduced to enhance the surface quality and high-temperature performance of laser directed energy deposition (LDED) Inconel 718 samples. The surface morphology and microstructure were analysed before and after laser polishing, and the result showed that the surface roughness was reduced by 97.4% and the grains of the recrystallized layer were refined through this post-treatment. Furthermore, the wear resistance, corrosion behaviour, and tensile strength of the laser polishing LDED Inconel 718 samples at the high-temperature of 650°C were investigated detailed. The result showed that the high-temperature tensile strength saw an increase of 14.97%, while both the high-temperature wear resistance and corrosion performance of Inconel 718 exhibited improvements compared to the as-fabricated samples.

engineering, manufacturing,materials science, multidisciplinary

What problem does this paper attempt to address?

### Problems the Paper Aims to Solve

This paper aims to improve the performance of Inconel 718 samples manufactured by Laser Directed Energy Deposition (LDED) under high-temperature conditions through hybrid laser polishing post-processing technology. Specifically, the study focuses on the following aspects:

1. **Surface Quality Improvement**: Significantly improving the surface roughness of LDED Inconel 718 samples through hybrid laser polishing technology. Experimental results show that the surface roughness of the treated samples was reduced by 97.4%, and grain refinement was achieved.

2. **Enhanced High-Temperature Performance**: Investigating the wear resistance, corrosion resistance, and tensile strength of LDED Inconel 718 samples treated with laser polishing at a high temperature of 650°C. The results indicate that the high-temperature tensile strength increased by 14.97%, and both high-temperature wear resistance and corrosion resistance were also improved.

3. **Microstructure and Phase Distribution Analysis**: Characterizing the samples using Scanning Electron Microscopy (SEM) and Energy Dispersive Spectroscopy (EDS) to analyze the effects of different treatment processes on the material's microstructure and phase distribution.

In summary, this paper mainly explores the effectiveness and mechanisms of hybrid laser polishing technology in enhancing the high-temperature performance of Inconel 718 alloy.