Carbothermal-sulfurization of TiO2 into Ti2SC MAX phase in TiO2/C/FeS2 ternary system

Sheng Pang,Zhenqian Zhang,Liangwei Cong,Youpeng Xu,Guoyu Qian,Dong Wang,Laishi Li,Yusheng Wu,Zhi Wang

DOI: https://doi.org/10.1016/j.ceramint.2023.09.225

IF: 5.532

2023-09-01

Ceramics International

Abstract:The conventional method for synthesizing Ti2SC depends on the reaction between TiS and TiC, which requires the utilization of costly Ti, TiC, or TiS2 powders. Utilizing TiO2 as the raw material for the synthesis of Ti2SC enables the cost-effective preparation of this compound. However, the optimization of the TiO2/C/XnSm (sulfides) system is of utmost importance when aiming to synthesize Ti2SC through carbothermal-sulfurization of TiO2, as the formation temperature of TiS and TiC greatly depends on the XnSm. In this study, the identification of the thermodynamically dominant region for the formation of TiS and TiC in the TiO2/C/XnSm systems was conducted by utilizing various sulfides (63 types). Considering factors such as the challenges associated with removing by-products, accessibility, and toxicity, FeS2 was ultimately chosen as a highly promising candidate. Thanks to the low melting point of FeS2, Ti3O5, the preliminary carbothermal reduction product of TiO2, has achieved rapid-deep deoxidation and phase reconstruction processes in the molten phase. Meanwhile, unlike the conventional solid-solid sintering reaction, which often results in residual reactants that are challenging to eliminate. This novel one-step phase transformation process that occurs in the molten phase exhibits minimal impurity phases, apart from the by-product Fe. Ti2SC with a purity greater than 99 wt% was obtained when the TiO2/C/FeS2 was pickled to remove Fe after sintering at 1600 °C for 5 min. This work will provide the theoretical basis and a new path for the low-cost preparation of sulfur-containing MAX phases.

materials science, ceramics