Impact Behavior and Residual Strength of PEEK/CF-Laminated Composites with Various Stacking Sequences

Alexander V. Eremin,Mikhail V. Burkov,Alexey A. Bogdanov,Anastasia A. Kononova,Pavel S. Lyubutin

DOI: https://doi.org/10.3390/polym16050717

IF: 5

2024-03-07

Polymers

Abstract:Carbon fiber-reinforced composites are popular due to their high strength and light weight; thus, the structures demonstrate high performance and specific strength. However, these composites are susceptible to impact damage. The objective of this research was to study the behavior of carbon fiber-reinforced laminates based on a polyetheretherketone (PEEK) matrix with six stacking sequences under static and impact loading. Four-point bending, short-beam bending, drop weight impact, and compression after impact tests were carried out. The results were complemented with digital shearography to estimate the damaged areas. Finite element modeling served to assess the failure mechanisms, such as fiber and matrix failure, in different layers due to tension of compression. Three behavior pattern of layups under drop-weight impact were found: (i)—energy redistribution due to mostly linear behavior (like a trampoline) and thus lower kinetic energy absorption for damage initiation, (ii)—moderate absorption of energy with initiation and propagation of concentrated damage with depressed redistribution of energy in the material, (iii)—moderate energy absorption with good redistribution due to initiation of small, dispersed damage. The results can be used to predict the mechanical behavior of composites with different stacking sequences in materials for proper structural design.

polymer science

What problem does this paper attempt to address?

The problem that this paper attempts to solve is to study the influence of different stacking sequences on the mechanical behavior and residual strength of polyetheretherketone (PEEK)/carbon fiber (CF) laminated composites under static and impact loads. Specifically, the author hopes to evaluate the damage behavior and residual strength of PEEK/CF laminated composites with six different stacking sequences after being impacted through experiments and finite - element simulations, thereby providing a basis for the design and application of materials.

### Main problem summary:
1. **Impact damage behavior**: Study the damage mechanisms of PEEK/CF laminated composites with different stacking sequences under impact loads.
2. **Residual strength**: Evaluate the mechanical properties that these materials can still maintain after being impacted.
3. **Influence of stacking sequence**: Explore how different fiber arrangements affect the impact resistance and residual strength of materials.

### Experimental methods:
- **Four - point bending test**: Evaluate the bending properties of materials.
- **Short - beam bending test**: Measure the short - beam strength of materials to characterize the inter - laminar shear strength.
- **Drop - weight impact test**: Simulate actual impact conditions and study the damage behavior of materials.
- **Post - impact compression test**: Evaluate the residual compressive strength of materials after impact.
- **Digital shear measurement**: Used to estimate the damaged area after impact.
- **Finite - element simulation**: Use the Hashin criterion and Benzeggagh - Kenane criterion for numerical simulation to predict the failure modes of materials.

Through these experiments and simulations, researchers hope to reveal the specific influence of different stacking sequences on the mechanical properties of PEEK/CF laminated composites and provide theoretical support for optimizing the design of composite materials.