Abstract:Two-dimensional (2D) graphitic carbon nitride (g-CN) is a promising anode material for sodium ion batteries (SIBs), but its insufficient interlayer spacing and poor electronic conductivity impede its sodium storage capacity and cycling stability. Herein, we report the fabrication of a fullerene (C60)-modified graphitic carbon nitride (C60@CN) material which as an anode material for SIBs shows a high reversible capacity (430.5 mA h g−1 at 0.05 A g−1, about 3 times higher than that of pristine g-CN), excellent rate capability (226.6 mA h g−1 at 1 A g−1) and ultra-long cycle life (101.2 mA h g−1 after 5000 cycles at 5 A g−1). Even at a high active mass loading of 3.7 mg cm−2, a reversible capacity of 316.3 mA h g−1 can be obtained after 100 cycles. Such outstanding performance of C60@CN is attributed to the C60 molecules distributed in the g-CN nanosheets, which enhance the electronic conductivity and prevent g-CN sheets from restacking, thus resulting in enlarged interlayer spacing and exposed edge N defects (pyridinic N and pyrrolic N) for sodium-ion storage. Furthermore, a sodium-ion full cell combining C60@CN anode and NVPF@rGO cathode provides high Coulombic efficiency (>96.5%), exceptionally high energy density (359.8 W h kganode−1 at power density of 105.1 W kganode−1) and excellent cycling stability (89.2% capacity retention over 500 cycles at 1 A ganode−1). This work brings new insights into the field of carbon-based anode materials for SIBs.

Efficient Electron Injection into Graphullerene Enables Reversible NaC2 Sodium Storage

Engineering Capacitive Contribution in Nitrogen-Doped Carbon Nanofiber Films Enabling High Performance Sodium Storage

Real-time Imaging of Na+ Reversible Intercalation in "janus" Graphene Stacks for Battery Applications

Solvated Sodium Storage Via a Coadsorptive Mechanism in Microcrystalline Graphite Fiber

Binding Sulfur-Doped Nb2O5 Hollow Nanospheres on Sulfur-Doped Graphene Networks for Highly Reversible Sodium Storage

Na(+) intercalation pseudocapacitance in graphene-coupled titanium oxide enabling ultra-fast sodium storage and long-term cycling

A promising anode material for sodium-ion battery with high capacity and high diffusion ability: graphyne and graphdiyne

Sodium into γ-Graphyne Multilayers: An Intercalation Compound for Anodes in Metal-Ion Batteries

Impact of Surface Modification on the Lithium, Sodium, and Potassium Intercalation Efficiency and Capacity of Few-Layer Graphene Electrodes

Superior Cycle Stability of Nitrogen-Doped Graphene Nanosheets for Na-ion Batteries

Fullerene‐Intercalated Graphitic Carbon Nitride as a High‐Performance Anode Material for Sodium Ion Batteries

Assembly of Na3V2(PO4)2F3@C nanoparticles in reduced graphene oxide enabling superior Na+ storage for symmetric sodium batteries

Codoped Holey Graphene Aerogel by Selective Etching for High-Performance Sodium-Ion Storage

A Promising Carbon/g‐C3N4 Composite Negative Electrode for a Long‐Life Sodium‐Ion Battery

Amorphous SnSe quantum dots anchoring on graphene as high performance anodes for battery/capacitor sodium ion storage

Crumpled Graphene with Graded Interlayer Spacing for High-Rate Na+ Storage

Synthesizing Porous NaTi2(PO4)3 Nanoparticles Embedded in 3D Graphene Networks for High-Rate and Long Cycle-Life Sodium Electrodes.

Capacitive Sodium-Ion Storage Based on Double-Layered Mesoporous Graphene with High Capacity and Charging/Discharging Rate.

Novel Graphitic Sheets with Ultralong Cycling, Ultrafast Rate, and High Capacity for Sodium Storage

Mechanically Exfoliated Graphite for Highly Reversible Na‐Storage with Carbon Coated Na3V2(PO4)3 Cathode with Low‐Temperature Conditions

Honeycomb-kagome FSL-graphene: A carbon allotrope as an ultra-high capacity anode material for fast-rechargeable sodium-ion battery