Fullerene‐Intercalated Graphitic Carbon Nitride as a High‐Performance Anode Material for Sodium Ion Batteries

Pengju Li,Yanglin Shen,Ximing Li,Wenhuan Huang,Xing Lu

DOI: https://doi.org/10.1002/eem2.12200

2021-04-15

Abstract:<p>Two-dimensional (2D) graphitic carbon nitride (g-CN) is a promising anode material for sodium ion batteries (SIBs), but its insufficient interlayer spacing and poor electronic conductivity impede its sodium storage capacity and cycling stability. Herein, we report the fabrication of a fullerene (C₆₀)-modified graphitic carbon nitride (C₆₀@CN) material which as an anode material for SIBs shows a high reversible capacity (430.5 mA h g⁻¹ at 0.05 A g⁻¹, about 3 times higher than that of pristine g-CN), excellent rate capability (226.6 mA h g⁻¹ at 1 A g⁻¹) and ultra-long cycle life (101.2 mA h g⁻¹ after 5000 cycles at 5 A g⁻¹). Even at a high active mass loading of 3.7 mg cm⁻², a reversible capacity of 316.3 mA h g⁻¹ can be obtained after 100 cycles. Such outstanding performance of C₆₀@CN is attributed to the C₆₀ molecules distributed in the g-CN nanosheets, which enhance the electronic conductivity and prevent g-CN sheets from restacking, thus resulting in enlarged interlayer spacing and exposed edge N defects (pyridinic N and pyrrolic N) for sodium-ion storage. Furthermore, a sodium-ion full cell combining C₆₀@CN anode and NVPF@rGO cathode provides high Coulombic efficiency (&gt;96.5%), exceptionally high energy density (359.8 W h kg_anode⁻¹ at power density of 105.1 W kg_anode⁻¹) and excellent cycling stability (89.2% capacity retention over 500 cycles at 1 A g_anode⁻¹). This work brings new insights into the field of carbon-based anode materials for SIBs.</p>

materials science, multidisciplinary