Abstract:Cobalt-Rhenium (Co-Re)-based alloys are currently investigated as potential high-temperature materials with melting temperatures beyond those of nickel-based superalloys. Their attraction stems from the binary Co-Re phase diagram, exhibiting complete miscibility between Co and Re, whereby the melting temperature steadily increases with the Re-content. Thus, depending on the Re-content, one can tune the melting temperature between that of pure Co (1495 °C) and that of pure Re (3186 °C). Current investigations focus on Re-contents of about 15 at.%, which makes melting with standard equipment still feasible. In addition to solid solution strengthening due to the mixture of Co- and Re-atoms, particle strengthening by tantalum carbide (TaC) and titanium carbide (TiC) precipitates turned out to be promising in recent studies. Yet, it is currently unclear which of the two particle types is the best choice for high temperature applications nor has the strengthening mechanism associated with the monocarbide (MC)-precipitates been elucidated. To address these issues, we perform compression tests at ambient and elevated temperatures on the particle-free base material containing 15 at.% of rhenium (Re), 5 at.% of chromium (Cr) and cobalt (Co) as balance (Co-15Re-5Cr), as well as on TaC- and TiC-containing variants. Additionally, transmission electron microscopy is used to analyze the shape of the precipitates and their orientation relationship to the matrix. Based on these investigations, we show that TiC and TaC are equally suited for precipitation strengthening of Co-Re-based alloys and identify climb over the elongated particles as a rate controlling particle strengthening mechanism at elevated temperatures. Furthermore, we show that the Re-atoms are remarkably strong obstacles to dislocation motion, which are overcome by thermal activation at elevated temperatures.

Chemical and Structural Analysis of Newly Prepared Co-W-Al Alloy by Aluminothermic Reaction

Effect of Process Parameters on Microstructure and Properties of AlCoCrFeNi-WC-WS2 Composite Coating Prepared by Laser Cladding

Effect of Submicron SiC Particles on the Properties of Alcocrfeni High Entropy Alloy Coatings

Co–Al2O3 nanocomposites powder prepared by electroless plating

Preparation of ti-al based nanophase composite powder by mechanical alloying

Preparation of Ti/Al based nanophase composite powder by mechanical alloying

Fabrication of nanocrystalline supersaturated W–Al alloys with enhanced thermal stability and high sinterability

Microstructural Modelling Solution for Complex Co Based Alloys and Coatings

Investigation of the Structure and Properties of a Coating from a High-Entropy FeCoCrNiMn Alloy Obtained by a Wire Arc Additive Manufacturing

Microstructures and Properties of WC-10 wt.%CoCrFeNiAlx Composite Cemented Carbides

Influence of the Al Content on the Properties of Mechanically Alloyed CoCrFeNiMnXAl20-X High-Entropy Alloys

Crystallization behavior of ternary γ–γ′ Co–Al–W alloy

Preparation and characterisation of the Al-Cr-Fe-Mn-Mo high-entropy alloy reinforced by in-situ formed carbides

On the remarkable thermal stability of nanocrystalline cobalt via alloying

Polymorphism of High-Temperature Aluminothermic Synthesis Products in the Ni–Al–Co System

Characterization of Al-Co-Cr-Fe-Mn-Ni High-Entropy Alloy Coating Fabricated onto AA5083 Using Wire-Arc Additive Manufacturing

Thermogravimetric investigations of new γ-γ′ cobalt-based superalloys

Investigation of TaC and TiC for Particle Strengthening of Co-Re-Based Alloys

Preparation of the AlTiNiCuCox system high-entropy alloys and structural analysis

Microstructure Characteristics of Fe-Al Intermetallic Compound Coating Synthesized by Light Beam Alloying

Novel Ni–Co-based superalloys with high thermal stability and specific yield stress discovered by directed energy deposition