Abstract:BACKGROUND The emission of NOx can causes serious environmental pollution and endangers human health. In recent years, the selective catalytic reduction of NO with NH3 (NH3-SCR) technology has been widely studied and adopted to reduce the production and emissions of NOx during many technologies. RESULTS A series of Mn-Ce-Co-x/Ti-C,N catalysts were prepared by the impregnation method, and low-temperature NH3-SCR was studied. The results show that support modification (Ti-C,N) can broaden the operation temperature window of the catalyst (NO conversion >95%: Mn-Ce/TiO2 catalyst, 160-320 degrees C; Mn-Ce/Ti-C,N catalyst, 140-320 degrees C). The doping of Co further improves the low-temperature NH3-SCR of the catalyst. When n(Co):n(Ti) = 0.05, the catalyst has the best catalytic performance with the NO conversion reaches 100% at 100 degrees C. CONCLUSION Temperature-programmed reduction (H-2-TPR) and temperature-programmed desorption (NH3-TPD) results showed that Ti-C,N can improve the redox ability but reduces the surface acidity. Co-doping has no effect on surface acidity, but the redox ability is further improved. A suitable amount of Co-doping is beneficial to the optimal catalytic activity of Mn-Ce-Co-0.05/Ti-C,N catalyst. This suggests a balance between redox properties and surface acidity. Especially for the strong redox ability, it can promote the oxidation of NO to NO2, and promote low-temperature NH3-SCR through the 'fast SCR' pathway. X-ray photoelectron spectroscopy results of the highest chemisorbed oxygen (O-alpha) concentration and relative atomic ratio (Mn4+/Mnn+, Ce3+/Cen+ and Co3+/Con+) confirmed the above conclusion. Both the Langmuir-Hinshelwood (L-H) and Eley-Rideal (E-R) mechanisms occurred in the NH3-SCR reaction over the Mn-Ce-Co-0.05/Ti-C,N catalyst. (c) 2021 Society of Chemical Industry

Er-modified MnO for selective catalytic reduction of NO with NH3 at low temperature: Promoting effect of erbium on catalytic performance

Tailoring the Proceeding of the NH3-SCO and NH3-SCR Reactions over FeOx Catalysts by Modifying with NbOx

Mnox/Ceo2/Sio2 Catalysts Prepared by Adsorption Phase Reaction Technique for Selective Catalytic Reduction of Nox at Low-Temperature

Enhancement effects of Er modification on comprehensive performance of FeMn/TiO2 catalysts for selective reduction of NO with NH3 at low temperature

Promoting Metal Oxides–zeolite Electron Interaction on MnCeOx/HY Catalyst for Boosting Nitrogen Oxides Reduction

C,N‐modified TiO2‐supported Mn–Ce–Cox‐based Catalyst for Low‐temperature NH3‐SCR

Low Temperature Selective Catalytic Reduction Of No With Nh3 Over Mn-Fe Spinel: Performance, Mechanism And Kinetic Study

Selective catalytic reduction of NO with NH3 over MnOx-CeO2 catalysts: The great synergy between CeO2 and crystalline phase of Mn3O4

Insight into the Promoting Role of Er Modification on SO2 Resistance for NH3-SCR at Low Temperature over FeMn/TiO2 Catalysts

Si-modified Mn-Ce oxide catalyst for selective catalytic reduction of NOx with NH3 at low temperature

Sm-MnO catalysts for low-temperature selective catalytic reduction of NO with NH3: Effect of precipitation agent

Promotional effect of rare earth-doped manganese oxides supported on activated semi-coke for selective catalytic reduction of NO with NH3

Insights on the Mechanism of Enhanced Selective Catalytic Reduction of NO with NH3 over Zr-doped MnCr2O4: A Combination of in Situ DRIFTS and DFT

Doping effect of rare earth metal ions Sm3+, Nd3+ and Ce4+ on denitration performance of MnO catalyst in low temperature NH3-SCR reaction

Eley−Rideal Path Enhanced Nh3-Scr: Central Fe Atoms Activation for Electron Transfer Promotion

Ceria modified MnOx/TiO2 as a superior catalyst for NO reduction with NH3 at low-temperature

Adjustment of operation temperature window of Mn-Ce oxide catalyst for the selective catalytic reduction of NOx with NH3

Activity Improvement of Mn/Al2O3 for NH3-SCR Reaction via the Rare-Earth (Ce, La, Nd and Y) Oxides Modification

Mechanism and Kinetics Study on Low-Temperature NH3-SCR over Manganese–Cerium Composite Oxide Catalysts

Low-temperature Selective Catalytic Reduction of NO with NH3 over MnCe Oxides Supported on TiO2 and Al2O3: A Comparative Study

Novel Mn-Ce-Ti Mixed-Oxide Catalyst for the Selective Catalytic Reduction of NOx with NH₃.