Abstract:We report detailed degradation and rejuvenation studies of AC electroluminescence (EL) of the phosphor ZnS:Cu,Cl, aiming to better understand the physical mechanisms that control EL emission. We find that the AC EL emission spectra vary considerably with the AC driving frequency but all spectra can be fit to a sum of four Gaussians. During degradation, although there is a large overall decrease in amplitude, the shape of the emission spectra measured at a given AC frequency does not change. Annealing the samples after they are significantly degraded can rejuvenate the phosphors with a maximum rejuvenation occurring (for fixed annealing times) near 180 °C. Further, these test cells can be degraded and rejuvenated multiple times. However studies at slightly higher annealing temperatures (240 °C) show significant thermal degradation and, perhaps more importantly, a change in the spectral shape; this likely indicates that two distinct mechanisms are then operative. In extended x-ray absorption fine structure (EXAFS) experiments we find that the CuS nanoprecipitates in the ZnS host (∼ 75% of the Cu is in the CuS precipitates) do not change significantly after the 240 °C anneal; these experiments also provide a more detailed comparison of the local structure about Cu in pure CuS, and in ZnS:Cu,Cl. In addition, the EXAFS experiments also place an upper limit on the fraction of possible interstitial Cu sites, proposed as a blue emission center, at less than 10%. The combined experiments place strong constraints on the mechanisms for degradation and rejuvenation and suggest that EL degradation is most likely caused by either Cu or Cl diffusion under high E-fields, while thermal diffusion at slightly elevated temperatures without E-fields present, re-randomizes the (isolated) dopant distributions. Higher T anneals appear to damage the sharp tips on the precipitates.

Opto-impedance spectroscopy and equivalent circuit analyses of AC powder electroluminescent devices

Experimental study of excitation efficiency distribution in low-voltage-driven thin film electroluminescent devices

Experimental Study of Low-Voltage -Driven Thin Film Electroluminescence Mechanism

Spin-dependent Kinetics of Polaron Pairs in Organic Light-Emitting Diodes Studied by Electroluminescence Detected Magnetic Resonance Dynamics

Impact of surface polarization and ion accumulation on electroluminescence for methylammonium lead bromide light emitting diodes

Investigation of Energy Transfer and Charge Trapping in Dye-Doped Organic Light-Emitting Diodes by Magneto-Electroluminescence Measurement

Electroluminescence Performance Optimization of Films based on the Change of Macroscopic Structure and Microscopic Calculation

Photoluminescent and Electroluminescent Properties of DCM-1 Dispersed Poly(p-Phenylene Vinylene) Derivatives

Degradation and rejuvenation studies of AC electroluminescent ZnS:Cu,Cl phosphors

Surface Electroluminescence Phenomena from Polymer under AC Voltage

Theoretical Investigation of High-Efficiency Organic Electroluminescent Material: HLCT State and Hot Exciton Process

Field-dependent properties of electroluminescent devices based on DCM-doped poly(p-phenylene vinylene) derivatives

Surface Electroluminescence Phenomena of Insulating Polymers

Electroluminescence and Surface Trap Distribution in Polymeric Insulation

Influence of Sensitizer on Organic Electroluminescence

The influence of the concentration of Er3+ ions on the characteristics of AC-electroluminescence in ZnS:ErF3 thin films

Detection of defect-induced luminescence in epoxy-based insulation materials via phase-resolved photon counting method

Study on ZnGa2O4:Cr3+ A.c. Powder Electroluminescent Device

Enhancing light emission in flexible AC electroluminescent devices by tetrapod-like zinc oxide whiskers

Influence of the Phosphor Layer Composition on Flexible Electroluminescent Device Performance

Electric Field Evolution of Charge and Energy Transfer in Molecule-Doped Polymer Light-Emitting Diodes