Abstract:Stellite 6 is a Co-based alloy with excellent wear and corrosion resistance, resulting in it frequently being used as a hard-facing material. The main defect that occurs in the hard-facing process is the peeling of the hard-facing layer, which is caused by thermal stress due to differences in thermal expansion coefficients. This peeling phenomenon can be prevented by using a material with an intermediate coefficient of thermal expansion as a buffer layer. Component surfaces are strengthened through a technique called hard-facing, which increases the components' resistance to wear. In order to increase the wear and corrosion resistance of metal components, a high-hardness substance is usually coated onto their surface. Grinding is carried out to smooth the surface after the material is welded onto the base component. Small pieces, also referred to as "scrap", are frequently produced during this surface machining procedure. In the hard-facing process, scrap containing a mixture of base material and Stellite 6 is generated during material processing. If this scrap can be used as a buffer layer, the cost of raw materials can be reduced through the recycling of resources, and the overall energy consumption for recycling can be reduced because the process of separating Stellite 6 from the scrap is eliminated. In this study, the physical properties of Stellite 6 with Fe added were explored to determine whether the scrap produced could be used as a buffer layer. When iron was added to the mixture, the amount of carbide decreased, in addition to the wear resistance and hardness decreasing. Regarding the thermal expansion coefficient, the thermal expansion coefficient of Stellite 6 was found to be 15.879 μm/m·°C at 300 °C, and that of Stellite 6 with 40% Fe added was found to be 14.313 μm /m·°C at 300 °C. The thermal expansion coefficient of carbon steel is reported to be 12.8 μm /m·°C at 300 °C; thus, Stellite 6 with 40% Fe can be used as a buffer layer for Stellite 6 and carbon steel because of its suitable thermal expansion coefficient.

Wear Resistance of Stellite 6 Coatings at High Temperature

Corrosion and erosion performance of HVOF/TiAlN PVD coatings and candidate materials for high pressure gate valve application

High-temperature wear behavior of HVOF sprayed, laser glazed, and laser cladded Stellite 6 coatings on stainless steel substrate

Optimization and high-temperature wear characterization of Stellite alloy claddings developed using TIG welding on 56NiCrMoV7 die steel

Microstructure, hardness, and wear resistance at room and high temperature of Stellite-6/WC-6Co coatings deposited by laser cladding process

Microstructure, hardness and slurry erosion-wear behaviors of high-speed laser cladding Stellite 6 coatings prepared by the inside-beam powder feeding method

Experimental investigations on the chlorine-induced corrosion of HVOF thermal sprayed Stellite-6 and NiAl coatings with fluidised bed biomass/anthracite combustion systems

Microstructure Evolution and Failure Behavior of Stellite 6 Coating on Steel after Long-Time Service

Microstructure and mechanical properties of Stellite 6 alloy coating metallurgically bonded to 304 stainless steel by DED-LB technology

Microstructure and wear resistance of in-situ TiC reinforced Stellite 6 coating using PTA cladding

Microstructure and Erosional Behavior of Erosion-Resistant Coatings of Super-Critical Boiler Pipes

Effects of Isothermal Aging Process on Microstructure and Mechanical Properties of Stellite 6 Coatings by Plasma Arc Cladding

High temperature tribological behavior of atmospheric plasma-sprayed CoCrFeNiW0.3 + 5 at% C high-entropy alloy coating

High-temperature dry sliding wear behavior of additively manufactured austenitic stainless steel (316L)

High-temperature tribological performance of functionally graded Stellite 6/WC metal matrix composite coatings manufactured by laser-directed energy deposition

CORROSION BEHAVIOR OF SUPER-AUSTENITIC STAINLESS STEEL AL-6XN IN SUPERCRITICAL WATER

A comparative investigation of the effects of temperature on the oxidation resistance of high-velocity oxy-fuel coating on AISI316L

Wear behaviour and microstructural characteristics of cold sprayed nickel-alumina coatings on boiler steel

Exploring the wear mechanism of surface hardfacing Stellite 6 alloy on the cast iron over the wide temperature range

Stellite-6/(WC+TiC) Composite Coatings Produced by Laser Alloying on S355 Steel

The Effect of Fe on the Mechanical Properties of Stellite 6