Abstract:Zn–Ni, Zn–Co and Zn–Ni–Co coatings were electrodeposited on mild steel from an acidic chloride bath containing p-aminobenzenesulphonic acid (SA) and gelatin. These additives changed the phase content in the coatings, most likely as a result of their adsorption at the surface of the cathode. The effect of gelatin was more pronounced than that of SA. The Faradaic efficiency was higher than 90%. As the current density was increased or the bath temperature was decreased, the concentration of the nobler metal in the coating increased. Both concentrations of Ni and Co in the ternary alloy increased as the applied current density was increased. Nickel and cobalt were found to have a synergistic catalytic effect. The thickness of all coatings increased as the applied current density was increased. The hardness increased with current density to a peak value, and then decreased. The rate of Zn deposition was heavily influenced by mass-transport limitation at high applied current densities, while the rates of Ni and Co deposition were not. The anomalous codeposition was explained by the great difference between the exchange current densities of Zn and the iron-group metal. Potentiodynamic polarization scans and electrochemical impedance spectroscopy showed that the corrosion resistance of the ternary Zn–Ni–Co alloy coatings was approximately 10 times higher than that of Zn–Ni and 7 times higher than that of Zn–Co. The improved corrosion resistance of the ternary alloy was attributed to its surface chemistry, phase content, texture, and surface morphology. The ternary Zn–Ni–Co coating may thus replace the conventional Zn–Ni and Zn–Co coatings in a variety of applications.

Electroless deposited ternary alloys: third element chemical state, localisation and influence on the properties. A short review

Electroless deposition of ternary Ni–P alloy coatings containing tungsten or nano-scattered alumina composite on steel

Fabrication and performance of Ni-Co-P/Si3N4 electroplated composite coatings on al-si alloys

Study on Electroless Plating Ni-W-P Ternary Alloy with High Tungsten from Compound Complexant Bath

Electroplating and characterization of Zn–Ni, Zn–Co and Zn–Ni–Co alloys

Preparation of electroless deposition of NiTiZr(P) quaternary alloy and their properties

The Research on Coating of Electroless Ni-W-P Ternary Alloys

Influences of Co and process parameters on structure and corrosion properties of nanocrystalline Ni-W-Co ternary alloy film fabricated by electrodeposition at low current density

Preparation and Properties of Textured Ni–W Coatings Electrodeposited on the Steel Surface from a Pyrophosphate Bath

The effect of partial substitution of Ti with Zr, Cr or V in the Mg35Ti10Ni55 electrode alloy on its electrochemical performance

Electrodeposition of Ni-P composite coatings: A review

Electroplating and Physicochemical Properties of Zinc–Nickel Alloy Coatings from Ammonium Oxalate Electrolytes

Ni-P coatings electroplating - A review, Part I: Pure Ni-P alloy

Tribological behavior of electroless Ni-B ternary and quaternary coatings with inclusion of W and Mo

Microstructure and Electrochemistry Behavior of Ni-Cu-P Ternary Nickel-Based Amorphous Coating

Influence of the Contents of Refractory Components on the Corrosion Resistance of Ternary Alloys Based on Iron and Cobalt

Structure, Composition and Corrosion Resistance of Zn-Ni-P Alloys Electrodeposited from an Ionic Liquid Based on Choline Chloride

Studies of electroless Ni–Co–P ternary alloy on glass fibers

Electrodeposition of Ni-W-P alloy

A promising perspective in improving corrosion and wear resistance of plain steel through electrodeposition of thick Ni–Mo–W ternary alloy

Fabrication, thermal stability and microhardness of sputtered Ni–P–W coating