Abstract:Binary Mg–Ca alloys with various Ca contents were fabricated under different working conditions. X-ray diffraction (XRD) analysis and optical microscopy observations showed that Mg–xCa (x=1–3 wt%) alloys were composed of two phases, α(Mg) and Mg2Ca. The results of tensile tests and in vitro corrosion tests indicated that the mechanical properties could be adjusted by controlling the Ca content and processing treatment. The yield strength (YS), ultimate tensile strength (UTS) and elongation decreased with increasing Ca content. The UTS and elongation of as-cast Mg–1Ca alloy (71.38±3.01MPa and 1.87±0.14%) were largely improved after hot rolling (166.7±3.01MPa and 3±0.78%) and hot extrusion (239.63±7.21MPa and 10.63±0.64%). The in vitro corrosion test in simulated body fluid (SBF) indicated that the microstructure and working history of Mg–xCa alloys strongly affected their corrosion behaviors. An increasing content of Mg2Ca phase led to a higher corrosion rate whereas hot rolling and hot extrusion could reduce it. The cytotoxicity evaluation using L-929 cells revealed that Mg–1Ca alloy did not induce toxicity to cells, and the viability of cells for Mg–1Ca alloy extraction medium was better than that of control. Moreover, Mg–1Ca alloy pins, with commercial pure Ti pins as control, were implanted into the left and right rabbit femoral shafts, respectively, and observed for 1, 2 and 3 months. High activity of osteoblast and osteocytes were observed around the Mg–1Ca alloy pins as shown by hematoxylin and eosin stained tissue sections. Radiographic examination revealed that the Mg–1Ca alloy pins gradually degraded in vivo within 90 days and the newly formed bone was clearly seen at month 3. Both the in vitro and in vivo corrosion suggested that a mixture of Mg(OH)2 and hydroxyapatite formed on the surface of Mg–1Ca alloy with the extension of immersion/implantation time. In addition, no significant difference (p>0.05) of serum magnesium was detected at different degradation stages. All these results revealed that Mg–1Ca alloy had the acceptable biocompatibility as a new kind of biodegradable implant material. Based on the above results, a solid alloy/liquid solution interface model was also proposed to interpret the biocorrosion process and the associated hydroxyapatite mineralization.

Development of biodegradable Mg-Ca alloy sheets with enhanced strength and corrosion properties through the refinement and uniform dispersion of the Mg₂Ca phase by high-ratio differential speed rolling

Novel Mg-Al-Sn-Ca with enhanced mechanical properties and high corrosion rate via sub-rapid solidification for degradable magnesium alloy

Preparing Ca-P Coating on Biodegradable Magnesium Alloy by Hydrothermal Method: in Vitro Degradation Behavior

The Development of Binary Mg-Ca Alloys for Use As Biodegradable Materials Within Bone

Modification of Mechanical Properties and Corrosion Behaviors of Mg-Al-Sn-Ca Alloy Via Tuning Eutectic Phase by Sub-Rapid Solidification

Balancing the Strength and Ductility of Mg-6Zn-0.2Ca Alloy Via Sub-Rapid Solidification Combined with Hard-Plate Rolling

Degradable magnesium-based alloys for biomedical applications: The role of critical alloying elements

Spheroiding and Refining of Coarse CaMgSn Phase in Mg–Al–Sn–Ca Alloys for Simultaneously Improved Strength and Ductility Via Sub-Rapid Solidification and Controlled Rolling

Microstructure, Mechanical, and Corrosion Properties of Extruded Low-Alloyed Mg-xZn-0.2Ca Alloys

In Vitro Corrosion of As-Extruded Mg–Ca Alloys—the Influence of Ca Concentration

Mechanical and Corrosion Properties of Mg-Gd-Zn-Zr-Mn Biodegradable Alloy by Hot Extrusion

Enhancing mechanical properties and degradation performance of Mg−0.8wt.%Ca alloy by directional solidification

Microalloying Design of Biodegradable Mg-2Zn-0.05Ca Promises Improved Bone-Implant Applications

Microstructure, mechanical properties, and in vitro behavior of biodegradable Zn-1Mg-0.1Ca and Zn-1Mg-0.5Ca

Investigating the mechanical properties and corrosion resistance of extruded Mg-1Zn-xCaO (x=0, 0.5, 1.0 wt%) materials

Low-cost, Soluble, and Highly Ductile Mg–Bi–Ca Alloy Prepared by Extrusion and Annealing

A Corrosion-Resistant and Age-Hardenable Mg-Al-Mn-Ca-Ce Dilute Alloy with Fine-Grained Structure Processed by Controlled Rolling

Effect of Sc/Sm microalloying on microstructural and properties of Mg 2Zn-0.3Ca biodegradable alloy

Development of Biocompatible Bulk MgZnCa Metallic Glass with Very High Corrosion Resistance in Simulated Body Fluid

Microstructure, texture, and mechanical properties of Mg–4Zn–1Mn–xCa alloys and the fabrication of biomedical Mg thin-walled micro-tubes

Enhanced antimicrobial properties, cytocompatibility, and corrosion resistance of plasma-modified biodegradable magnesium alloys