Modification of Mechanical Properties and Corrosion Behaviors of Mg-Al-Sn-Ca Alloy Via Tuning Eutectic Phase by Sub-Rapid Solidification

Dawei Wang,Kejun Dong,Jiawei Liang,Fuyong Cao,Min Zha,Dongsong Wei,Hu Zhao,Meixuan Li,Cheng Wang,Hui–Yuan Wang
DOI: https://doi.org/10.2139/ssrn.3980037
2021-01-01
Abstract:Coarse eutectic phases generally exist in cast alloys and have dramatic effects on mechanical properties and corrosion behaviors. Therefore, it would be convenient and feasible to modify the mechanical properties and corrosion behaviors via tuning the eutectic phase. Herein, sub-rapid solidification (SRS) is employed to modify the microstructure, especially the eutectic phase of Mg-4.5Al-1.5Sn-0.5Ca alloy. Our results reveal that SRS followed by homogenization treatment not only reduces the grain size of α-Mg matrix, but also spheroidizes and refines the large stick-like CaMgSn phase to ~1 μm. The pronounced structure modification leads to a superior strength-ductility synergy of SRS alloy, i.e., an ultimate tensile strength (UTS) of ~236 MPa and an elongation to failure (Ɛf) of ~24%, in comparison to the alloy prepared via conventional solidification, with an UTS of ~220 MPa and an Ɛf ~21%. Moreover, the homogenized SRS alloy exhibits homogeneous corrosion with an increased corrosion rate of ~145 mm y-1 and 883 mm y-1 at 25 and 50 °C, respectively. It is mainly due to the large contact area and short distance between CaMgSn and α-Mg matrix derived from the refined CaMgSn particles in SRS alloy. Our work proposes a short-route and low-cost process, i.e., SRS followed by homogenization treatment, for preparing Mg alloys with enhanced mechanical properties and desirable corrosion behaviors, which might be promising for applications as degradable engineering materials.
What problem does this paper attempt to address?