Abstract:REBCO coated conductors are now being used for building very high-field magnets with large electromagnetic stresses, both expected ones due to transport current × stresses and additional stresses resulting from the large screening currents inherent in wide tapes. Post mortem analyses of several recent test coils operated above 40 T show that significant conductor plastic deformation occurs, even for JBR stresses well below the ~1 GPa yield of the Hastelloy substrate of the conductor. To investigate these deformation mechanisms, conductors were unwound after coil test and carefully examined with respect to their length-wise Ic which revealed many areas of local damage. Regions of interest were examined by metallographic cross-section, Hall microscopy, magneto-optic imaging and scanning electronic microscopy. Important damage frequently occurred to the outer edges of pancakes in the coil ends, which were often plastically deformed over the whole turn circumference, especially when this outer edge was a slit edge. Internal conductor damage was also seen, especially delamination between the buffer and REBCO layers at slit edges. Careful sectioning of the tape at ~10 mm intervals showed that the plastic deformation of the turns was complex and variable around the turn circumference, with tape cross-sections that exhibited continuous shape change in the outer turns. The bending center line of tapes often shifted from the tape center line toward the edge closest to the coil center, indicating asymmetric effects of transport and screening current stresses across the conductor width. A surprising and vital result is that damage was prevalent when the slit edge was also the edge at which transport current flowed. This damage was absent when the transport current flowed at the not-slit edge, implying great sensitivity of the effect of screening current stresses to localized conductor damage.

Study of delamination in REBCO coated conductor by transmission electron microscopy

REBCO delamination characterization by 90 degree peel test

In Situ Detection of Delamination and Critical Current Degradation Caused by the Thermal Stress in Epoxy Impregnated REBa2Cu3O7−δ Coils

Critical current degradation and delamination crack observation of epoxy-coated REBCO superconducting tapes after thermal cycles in liquid nitrogen

Delamination Avoidance in Epoxy Wet-Wound REBCO Coils by Release Agent Coating

Electromechanical degradation of REBCO coated conductor tapes under combined tension and torsion loading

Fabrication of Thick REBCO–Coated Conductors with High Performance on Metal Tapes by Pulsed Laser Deposition Process

Oxygen out-diffusion in REBCO coated conductor due to heating

Critical current degradation of commercial REBCO coated conductors under thermomechanical loads

A standardized measurement method and data analysis for the delamination strengths of YBCO coated conductors

Exploration of Correlation Between the Material Characteristics of the Copper Layer on the Electrical and Thermal Properties of REBCO Tape and Coil

Fabrication Technology of REBCO Coated Conductor and Its Development

Numerical Study on Mechanical Behavior and Electromechanical Properties of Solder-Jointed REBCO-Coated Conductors

High-field thermal transport properties of REBCO coated conductors

Fabrication and Electromagnetic Characterization of Ultrasmall Diameter REBCO Wires

Bending-Peeling Method to Research the Effect of Lateral Stress on Superconductivity of REBCO Tape at Liquid-Nitrogen Temperature

Advance in Long-Length REBCO Coated Conductors Prepared by Reel-to-Reel Metalorganic Solution and Ion-Beam-Assisted Deposition

Synergetic Evolution of the Microscopic Crystal Orientation and Macroscopic Superconducting Properties of REBCO Tape under Sever Deformation

Residual resistance ratio of Cu stabilizer in commercial REBCO tapes

Performance study of REBCO multi-filament tapes/ CORC cables prepared by reel-to-reel mechanical incision

Analyses of the plastic deformation of coated conductors deconstructed from ultra-high field test coils