Abstract:The technological and metallurgical requirements of material for highgradient superconducting cavities are described. High-purity niobium, as the preferred metal for the fabrication of superconducting accelerating cavities, should meet exact specifications. The content of interstitial impurities such as oxygen, nitrogen, and carbon must be below 10{\mu}g/g. The hydrogen content should be kept below 2{\mu}g/g to prevent degradation of the Q-value under certain cool-down conditions. The material should be free of flaws (foreign material inclusions or cracks and laminations) that can initiate a thermal breakdown. Defects may be detected by quality control methods such as eddy current scanning and identified by a number of special methods. Conventional and alternative cavity fabrication methods are reviewed. Conventionally, niobium cavities are fabricated from sheet niobium by the formation of half-cells by deep drawing, followed by trim machining and Electron-Beam Welding (EBW). The welding of half-cells is a delicate procedure, requiring intermediate cleaning steps and a careful choice of weld parameters to achieve full penetration of the joints. The equator welds are particularly critical. A challenge for a welded construction is the tight mechanical and electrical tolerances. These can be maintained by a combination of mechanical and radio-frequency measurements on halfcells and by careful tracking of weld shrinkage. The established procedure is suitable for large series production. The main aspects of quality assurance management are mentioned. Another cavity fabrication approach is slicing discs from the ingot and producing cavities by deep drawing and EBW. Accelerating gradients at the level of 35-45 MV.m-1 can be achieved by applying Electropolishing (EP) treatment....

Healing Gradient Degradation in Nb3Sn SRF Cavities Using a Recoating Method

Understanding and optimization of the coating process of the radio-frequency Nb 3 Sn thin film superconducting cavities using tin vapor diffusion method

Grain-boundary structure and segregation in Nb3Sn coatings on Nb for high-performance superconducting radiofrequency cavity applications

Analysis of RF losses and material characterization of samples removed from a Nb3Sn-coated superconducting RF cavity

Nanostructural features degrading the performance of superconducting radio frequency niobium cavities revealed by TEM and EELS

Analysis of Thermal Grooving Effects on Vortex Penetration in Vapor-Diffused Nb3Sn

Role of microstructure on flux expulsion of superconducting radio frequency cavities

SRF Cavity Fabrication and Materials

Improving Nb3Sn Cavity Performance Using Centrifugal Barrel Polishing

Analysis of post wet chemistry heat treatment effects on Nb SRF surface resistance

Development and Understanding of Nb$_3$Sn films for radiofrequency applications through a sample-host 9-cell cavity

Nb3Sn multicell cavity coating system at JLAB

Influence of Nb substrate morphology and atomic structure on Sn nucleation and early Nb 3 Sn growth

Fermilab experience of post-annealing losses in SRF niobium cavities due to furnace contamination and the ways to its mitigation: a pathway to processing simplification and quality factor improvement

First Results from Nb3Sn Coatings of 2.6 GHz Nb SRF Cavities Using DC Cylindrical Magnetron Sputtering System

Microstructural Refinement of Niobium for Superconducting RF Cavities

Feasibility Study on SRF Cavity Improvement by Doping Method

RF surface resistance tuning of superconducting niobium via thermal diffusion of native oxide

Development and characterization of Nb3Sn/Al2O3 superconducting multilayers for particle accelerators

Selective thermal evolution of native oxide layer in Nb and Nb3Sn-coated SRF grade Nb: An in-situ angular XPS study

Preservation of the High Quality Factor and Accelerating Gradient of Nb3Sn-coated Cavity During Pair Assembly