Abstract:We investigate the rf performance of several single-cell superconducting radio-frequency cavities subjected to low temperature heat treatment in nitrogen environment. The cavities were treated at temperature 120–165 °C for an extended period of time (24–48 h) either in high vacuum or in a low partial pressure of ultrapure nitrogen. The improvement in Q0 with a Q rise was observed when nitrogen gas was injected at ∼300 °C during the cavity cooldown from 800 °C and held at 165 °C , without any degradation in accelerating gradient over the baseline performance. The treatment was applied to several elliptical cavities with frequency ranging from 0.75 to 3.0 GHz, showing an improved quality factor as a result of low temperature nitrogen treatments. The Q rise feature is similar to that achieved by nitrogen alloying Nb cavities at higher temperature, followed by material removal by electropolishing. The surface modification was confirmed by the change in electronic mean free path and tuned with the temperature and duration of heat treatment. The decrease of the temperature-dependent surface resistance with increasing rf field, resulting in a Q rise, becomes stronger with increasing frequency and decreasing temperature. The data suggest a crossover frequency of ∼0.95 GHz above that the Q rise phenomenon occurs at 2 K. Some of these results can be explained qualitatively with an existing model of intrinsic field-dependence of the surface resistance with both equilibrium and nonequilibrium quasiparticle distribution functions. The change in the Q slope below 0.95 GHz may result from masking contribution of trapped magnetic flux to the residual surface resistance. https://doi.org/10.1103/PhysRevAccelBeams.27.062001 Published by the American Physical Society under the terms of the Creative Commons Attribution 4.0 International license. Further distribution of this work must maintain attribution to the author(s) and the published article's title, journal citation, and DOI. Published by the American Physical Society

Analysis of post wet chemistry heat treatment effects on Nb SRF surface resistance

Effect of high temperature heat treatments on the quality factor of a large-grain superconducting radio-frequency niobium cavity

Role of thermal resistance on the performance of superconducting radio frequency cavities

Effect of Successive Heat Treatment on the Performance of Superconducting Radio Frequency Niobium Cavities

A Path to Higher Q0 with Large Grain Niobium Cavities

Ultra-Low Surface Resistance via Vacuum Heat Treatment of Superconducting Radiofrequency Cavities

Evaluation of flux expulsion and flux trapping sensitivity of srf cavities fabricated from cold work Nb sheet with successive heat treatment

Influence of material parameters on the performance of niobium based superconducting RF cavities

The oxidation behaviors of high-purity niobium for superconducting radio-frequency cavity application in vacuum heat treatment

RF surface resistance tuning of superconducting niobium via thermal diffusion of native oxide

Field, frequency, and temperature dependencies of the surface resistance of nitrogen diffused niobium superconducting radio frequency cavities

Field, frequency and temperature dependence of the surface resistance of nitrogen diffused niobium superconducting radio frequency cavities

On the quest of low temperature nitrogen infusion relevant for superconducting Nb based radio-frequency cavities

Correlation of srf performance to oxygen diffusion length of medium temperature heat treated cavities

Surface Resistance Effects of Medium Temperature Baking of Buffered Chemical Polished 1.3 GHz Nine-Cell Large-Grain Cavities

Temperature, RF Field, and Frequency Dependence Performance Evaluation of Superconducting Niobium Half-Wave Cavity

Analysis of RF losses and material characterization of samples removed from a Nb3Sn-coated superconducting RF cavity

Fermilab experience of post-annealing losses in SRF niobium cavities due to furnace contamination and the ways to its mitigation: a pathway to processing simplification and quality factor improvement

Nitrogen and argon doping of niobium for superconducting radio frequency cavities: a pathway to highly efficient accelerating structures

Improvement and protection of niobium surface superconductivity by atomic layer deposition and heat treatment

The Collaborative Effects of Intrinsic and Extrinsic Impurities in Low RRR SRF Cavities