Abstract:Thin Ga2O3 films were grown on Si (100) using trimethylgallium (TMG) and oxygen as the precursors through plasma-enhanced atomic layer deposition. The depositions were made over a temperature range of 80-250 degrees C with a growth per cycle of around 0.07 nm/cycle. Surface self-saturating growth was obtained with TMG pulse time >= 20 ms at a temperature of 150 degrees C. The root mean square surface roughness of the obtained Ga2O3 films increased from 0.1 nm to 0.3 nm with increasing the growth temperature. Moreover, the x-ray photoelectron spectroscopy analysis indicated that the obtained film was Ga-rich with the chemical oxidation states Ga3+ and Ga1+, and no carbon contamination was detected in the films after Ar+ sputtering. The electron density of films measured by x-ray reflectivity varied with the growth temperature, increasing from 4.72 to 5.80 g/cm(3). The transmittance of Ga2O3 film deposited on a quartz substrate was obtained through ultraviolet visible (UV-Vis) spectroscopy. An obvious absorption in the deep UV region was demonstrated with a wide band gap of 4.6-4.8 eV. The spectroscopic ellipsometry analysis indicated that the average refractive index of the Ga2O3 film was 1.91 at 632.8 nm and increased with the growth temperature due to the dense structure of the films. Finally, the I-V and C-V characteristics proved that the Ga2O3 films prepared in this work had a low leakage current of 7.2 x 10(-11) A/cm(2) at 1.0 MV/cm and a high permittivity of 11.9, suitable to be gate dielectric.

Electrical characterization of gadolinium oxide deposited by high pressure sputtering with in situ plasma oxidation

Anomalous thermal oxidation of gadolinium thin films deposited on silicon by high pressure sputtering

Optimization of gadolinium oxide growth deposited on Si by high pressure sputtering

Scavenging effect on plasma oxidized Gd$_2$O$_3$ grown by high pressure sputtering on Si and InP substrates

Analysis of the Electrical Properties and Current Transportation Mechanism of a Metal Oxide Semiconductor (MOS) Capacitor Based on HfGdO Gate Dielectrics

High-k gadolinium scandate on Si obtained by high pressure sputtering from metal targets and in-situ plasma oxidation

Comparison of Microstructure and Electrical Characteristics of Sputtering-Derived HfGdO/HfTiO and HfTiO/HfGdO Gate Stacks

Modulation of Interfacial and Electrical Properties of Hfgdo/Gaas Gate Stacks by Ammonium Sulfide Passivation and Rapid Thermal Annealing

High Pressure Sputtering For Kigh-k Dielectric Deposition. Is It Worth Trying?

Gadolinium scandate by high-pressure sputtering for future generations of high-k dielectrics

Towards metal electrode interface scavenging of rare-earth scandates: A Sc2O3 and Gd2O3 study

Low-Temperature Floating Plasma Oxidation of Poly-SiGe

Chemical, Optical, and Electrical Characterization of Ga2O3 Thin Films Grown by Plasma-Enhanced Atomic Layer Deposition

Optimization of scandium oxide growth by high pressure sputtering on silicon

Electrical Characterization of Ultrathin Single Crystalline Gd2O3/Si(100) with Pt Top Electrode

Electrical Characterization of Ultrathin Single Crystalline Gd<inf>2</inf>O<inf>3</inf>/Si(100) with Pt Top Electrode

Annealing of Gadolinium-Doped Ceria (GDC) Films Produced by the Aerosol Deposition Method

Enhanced Electrical Performance and Low Frequency Noise of In2O3 Thin-Film Transistors Using Al2O3/CeGdOx Bilayer Gate Dielectrics

Ge Surface Passivation by GeO 2 Fabricated by N 2 O Plasma Oxidation

Process Intensification and Performance Assessment of Sputtered Gadolinium Doped Ceria (GDC) Barrier Layer in Large-Area Solid Oxide Fuel Cell Short Stack

Phase Control of Magnetron Sputtering Deposited Gd2O3 Thin Films As High-Κ Gate Dielectrics