Abstract:Annealing Mg-implanted homoepitaxial GaN at temperatures above 1400 °C eliminates the formation of inversion domains and leads to improved dopant activation efficiency. Extended defects, in the form of inversion domains, contain electrically inactive Mg after post-implantation annealing at temperatures as high as 1300 °C (one GPa N2 overpressure), which results in a low dopant activation efficiency. Triple-axis x-ray data reveal that implant-induced strain is fully relieved after annealing at 1300 °C for 10 min, indicating that strain-inducing point defects formed during implantation have reconfigured and inversion domains are formed. However, annealing at temperatures of 1400–1500 °C (one GPa N2 overpressure) eliminates the presence of the inversion domains. While residual defects, such as dislocation loops, still exist after annealing at and above 1400 °C, chemical analysis at multiple dislocation loops shows no sign of Mg segregation. Meanwhile, an overall decreasing trend in the dislocation loop density is observed after annealing at the higher temperatures and longer times. Additionally, once inversion domains are formed and the samples are cooled to room temperature, they are shown to dissolve with subsequent annealing above 1400 °C. While such defects have been observed before, the important finding that such defects can be dissolved with a short, higher temperature step is key. Earlier work [Breckenridge et al., J. Appl. Phys. Lett. 118, 022101 (2021)] addressing electrical measurements of these types of samples showed that annealing at 1400 °C leads to a dopant activation efficiency that is an order of magnitude higher than that observed at 1300 °C. This work complements earlier work by identifying the inversion domains, which incorporate Mg, and points to the benefits, in terms of defect density and p-type dopant activation, of using higher temperature (>1400 °C) annealing cycles to activate Mg in GaN, even if the Mg-containing inversion domains had been formed during lower temperature annealing.

Silicon Implantation and Annealing in $β$-Ga$_2$O$_3$: Role of Ambient, Temperature, and Time

Silicon implantation and annealing in β -Ga2O3: Role of ambient, temperature, and time

Silicon Ion Implant Activation in β-(Al0.2Ga0.8)2O3

Dopant Activation In Poly-Si1-Xgex At Low Temperature

The role of annealing ambient on diffusion of implanted Si in β-Ga2O3

Low-temperature Annealing of Polycrystalline Si/sub 1-X/ge/sub X/ after Dopant Implantation

Si Implantation in GaN at Elevated Temperatures

Structural and Electrical Characterizations of Si-implanted GaN with a High Dose at Elevated Temperatures

Characterization of the Interface Region During the Agglomeration of Silicon Nanocrystals in Silicon Dioxide

Selective Area Carrier Concentration Modulation of Single Crystal $\Beta$-Ga2o3 Film Through High Temperature Oxygen Annealing Process

Dopant Activation in Poly-SI/sub1-x/Ge/subx/ at Low Temperature

Dissolution of Mg-enriched defects in implanted GaN and increased p-type dopant activation

Optical Properties Revealing Annealing Behavior of High-Temperature He-Implantation Induced Defects in Silicon Carbide

Optimum Annealing Conditions for Boron Implanted Sige Epilayers

Effects of implementing dual-step nitrogen ambient for growth and post-deposition annealing of Ga2O3 films sputtered on silicon

Effects of Annealing Temperature on Buried Oxide Precipitates in He and O Co-Implanted Si

Annealing behavior of Si1-xGex/Si heterostructure formed by Ge+ implantation with X-ray diffraction

Electrical properties of silicon-implanted β-Ga2O3:Fe crystals

Surface roughening in ion implanted 4H-silicon carbide

Effects of Annealing on Surface Residual Impurities and Intrinsic Defects of Β-Ga2o3

Impact of an Annealing Atmosphere on Band-Alignment of a Plasma-Enhanced Atomic Layer Deposition-Grown Ga2O3/SiC Heterojunction