Abstract:In order to provide the necessary phase equilibria data for understanding the development of the Widmanstatten pattern in iron meteorites, we have redetermined the Fe-Ni-P phase diagram from 0 to 100 pct Ni, 0 to 16.5 wt pct P, in the temperature range 1100° to 550°C. Long term heat treatments and 130 selected alloys were used. The electron microprobe was employed to measure the composition of the coexisting phases directly. We found that the fourphase reaction isotherm, where α+ liq ⇌ γ+ Ph, occurs at 1000° ± 5°C. Above this temperature the ternary fields α+ Ph + liq and α+ γ+ liq are stable and below 1000°C, the ternary fields ⇌+ γ + Ph and γ + Ph + liq are stable. Below 875°C a eutectic reaction, liq → γ + Ph, occurs at the Ni-P edge of the diagram. Altogether nineteen isotherms were determined in this study. The phase boundary compositions of the two-and three-phase fields are listed and are compared with the three binary diagrams. The α + γ + Ph field expands in area in each isotherm as the temperature decreases from 1000°C. Below 800°C the nickel content in all three phases increases with decreasing temperature. The phosphorus solubility in α and γ decreases from 2.7 and 1.4 wt pct at 1000°C to 0.25 and 0.08 wt pct at 550°C. The addition of phosphorus to binary Fe-Ni greatly affects the α/α + γ and γ/α + γ boundaries below 900°C. It stabilizes the α phase by increasing the solubility of nickel (α/α +γ boundary) and above 700°C, it decreases the stability field of the γ phase by decreasing the solubility of nickel(@#@ γ/α + γ boundary). However below 700°C, phosphorus reverses its role in γ and acts as a γ stabilizer, increasing the nickel solubility range. The addition of phosphorus to Fe-Ni caused significant changes in the nucleation and growth processes. Phosphorus contents of 0.1 wt pct or more allow the direct precipitation ofa from the parent γ phase by the reaction γ ⇌ α + γ. The growth rate of the α phase is substantially higher than that predicted from the binary diffusion coefficients.

Pseudobinary Phase Diagrams of Eutectic Reaction for Pt‐containing and Pt‐free 718Plus Alloys

Solidification behavior of Pt-containing 718Plus superalloy

Phase Equilibria in the Fe-Al-Nb(-B) System at 700 °C

Experimental determination of the Ni–Ni5Zr eutectic point for binary Ni–Zr alloy phase diagram

Experimental determination of the phase equilibria of aluminum-rich Al−Li−Cu alloys

Phase Equilibria in the Au-Cu-In-Pd System at 500 °C and 800 °C: Experimental Study and Modeling

Fabricating the AuPdPt Ternary Nanophase Diagram at 800 °C to Guide the Exploration of Optimal Catalyst for N-Hexane Oxidation

Experimental and first-principles characterization of heterogeneous nucleation of η on the E(Al18Mg3Cr2) phase in the 7075 Al alloys

Experimental study on phase relations in the Al-Mo-Nb ternary system

Phase Equilibria of the Al-Li Binary System

Design Multicomponent Eutectic Alloys in the Co–Cr–Fe–Ni–Nb System Using Simple Mixing Method

First principles investigation of phase stability in the B-Pt alloy system

A new refractory Ni7Nb2 phase identified in Laves eutectic regions by TEM study

The ternary phase diagram, Fe-Ni-P

Effect of the precipitation of the η-Ni3Al0.5Nb0.5 phase on the microstructure and mechanical properties of ATI 718Plus

Tailored Time-Temperature Transformation Diagram for IN718 Alloy Obtained via Powder Bed Fusion Additive Manufacturing: Phase Behavior and Precipitation Dynamic

Phase Equilibria of the Sn-Sb Binary System

The Mineralogy of Pt-Fe alloys and phase relations in the Pt–Fe binary system

Growth mechanisms of eta phase in 718Plus alloy

Phase stability of a eutectic high entropy alloy under extremes of pressures and temperatures

Phase equilibria in Ni–Ti–Ta ternary system