Fracture Behavior and Mechanism of Nb-Si-Based Alloys with Heterogeneous Layered Structure

Sheng Wang,Xiaoli Wang,Zhiming Wang,Zhiping Sun,Weicheng Ye,Qihu Zhao

DOI: https://doi.org/10.3390/ma17112735

IF: 3.4

2024-06-05

Materials

Abstract:Novel Nb-Si-based alloys with heterogeneous layers that have the same composition (Nb-16 at.%Si) but different phase morphologies were designed in this work. Heterogeneous layered structure (HLS) was successfully fabricated in Nb-16Si alloys by layering composite powders after various degrees of mechanical alloying (6 h, 12 h, 18 h, and 24 h) alternately and subsequent spark plasma sintering (SPS). The influence of HLS on the fracture behavior at both room and elevated temperature was investigated via single-edge notched bending (SENB) and high-temperature compression, respectively. The results show that the diversified HLS is obtained by combining hard layers containing fine equiaxed crystals and/or soft ones with coarse lamellar niobium solid solution (Nbss). By affecting the crack propagation in SENB, HLS is favorable for improving the fracture toughness and exhibits a significant increase compared with the corresponding homogenous microstructure. Moreover, for the same HLS, a more excellent performance is achieved when the initial crack is located in the soft layer and extended across the interface to the hard one through crack bridging, crack deflection, crack branching, and shielding effect. Fracture starts in the soft layer (from powders of ball-milled for 12 h) of a 12–24 alloy, and a maximum KQ value (14.89 MPa·mm1/2) is consequently obtained, which is 33.8% higher than that of the homogeneous Nb-16Si alloy. Furthermore, the heterogeneous layered alloys display superior high-temperature compression strength, which is attributable to the dislocation multiplication and fine-grained structure. The proposed strategy in this study offers a promising route for fabricating Nb-Si-based alloys with optimized and improved mechanical properties to meet practical applications.

materials science, multidisciplinary,metallurgy & metallurgical engineering,physics, applied,chemistry, physical, condensed matter

What problem does this paper attempt to address?

The problem this paper attempts to address is improving the fracture toughness of Nb-Si based alloys at both room and high temperatures while maintaining their high strength. Specifically, the researchers designed a Nb-16Si alloy with a heterogeneous layered structure (HLS), prepared through different mechanical alloying times and subsequent spark plasma sintering (SPS) processes. This structure aims to improve the fracture toughness of the material by influencing the crack propagation path, thereby overcoming the inherent brittleness of Nb-Si based alloys.

### Main Issues of the Paper:
1. **Improving the Fracture Toughness of Nb-Si Based Alloys**:
- The researchers explored how to improve the fracture toughness of Nb-Si based alloys without significantly reducing their strength by designing a heterogeneous layered structure with different phases.
- The impact of HLS on fracture behavior at room and high temperatures was studied through single-edge notched bend (SENB) tests and high-temperature compression tests.

2. **Optimizing the Mechanical Properties of Nb-Si Based Alloys**:
- The researchers investigated the effect of different mechanical alloying times on the microstructure and mechanical properties of Nb-Si based alloys, particularly the impact of different layered structures on the crack propagation path.
- By adjusting the volume fraction and morphology of Nbss and silicides, the mechanical properties of the HLS alloy were optimized.

3. **Understanding the Crack Propagation Mechanism**:
- The researchers conducted a detailed analysis of the crack propagation path in different layered structures, including mechanisms such as crack deflection, branching, bridging, and shielding, which contribute to energy dissipation and improved fracture toughness.
- The fracture surfaces and crack propagation paths were observed and analyzed using scanning electron microscopy (SEM), revealing the fracture behavior of HLS alloys under different conditions.

### Main Conclusions:
- **The introduction of HLS significantly improved the fracture toughness of Nb-Si based alloys**, especially when the initial crack was located in the soft layer and propagated through the interface to the hard layer, showing better performance.
- **When the crack propagated from the 6-hour layer (soft layer) to the 24-hour layer (hard layer) in the 12-24 alloy, the fracture toughness reached a maximum value of 14.89 MPa·mm^1/2**, which is a 33.8% improvement over the homogeneous Nb-16Si alloy.
- **The HLS alloy also exhibited excellent performance in high-temperature compression tests**, attributed to dislocation proliferation and fine-grained structure.

In summary, this paper successfully improved the fracture toughness and high-temperature strength of Nb-Si based alloys by designing and preparing Nb-Si based alloys with a heterogeneous layered structure, providing a new approach to optimizing the mechanical properties of Nb-Si based alloys.