Abstract:We report an industrial compatible tunnel oxide passivated contact (TOPCon) structure on solar-grade p-type c-Si wafer as the rear emitter for high-efficiency solar cells, where the ultrathin silicon oxide (SiOx) is made by plasma-assisted oxidation and the P-doped n-type poly-Si (n+-poly-Si) contact layer by plasma-enhanced chemical vapor deposition (PECVD) of hydrogenated amorphous silicon (a-Si:H) with in-situ doping with PH3 and following the high-temperature annealing. The fabrication processes of SiOx and n+-poly-Si layers are systematically optimized. It is found that the optimized annealing temperature for the crystallization and dopant activation is in the range of 850 °C and 880 °C, which is higher than the similar structure with chemically oxidized SiOx (820 °C). In addition, the samples made with higher PH3/SiH4 doping ratio during the a-Si:H deposition need a lower annealing temperature to reach the similar dopant distribution within the samples made with lower doping ratio but annealed at higher temperature, it means that the optimized annealing temperature decreases with the increase of the PH3/SiH4 doping ratio during the deposition of a-Si:H precursor. The optimized process with post-hydrogenation yields excellent surface passivation on the p-type Si substrate with the implied open-circuit voltage (iVoc) of ∼742 mV, the single-side saturated recombination current density (J0) of ∼3.0 fA/cm2, the contact resistivity (ρc) of ∼2–4 mΩ cm2, and the effective minority carrier lifetime (τeff) of ∼1050 μs (Δn = 1 × 1015 cm-3). With these passivation parameters, a simulation study demonstrates the advantage of rear emitter over the conventional front emitter TOPCon solar cell with ∼22.8% achievable efficiency on solar-grade p-type wafers with current industrial constraints, and ∼24.9% on high quality p-type c-Si wafers with the optimized conditions in R&D laboratories. Our study suggests that the p-type c-Si solar cell with a rear n+-poly-Si TOPCon emitter is a viable structure for high-efficiency solar cell production.

Beyond the crystalline silicon solar cell mass-production—high energy-conversion-efficiency N-type back-junction front-contact and back-junction back-contact mono-crystalline silicon solar cells

Advancements in Passivation and Metallization Techniques for n-Type Monocrystalline Silicon Solar Cells

Numerical and experimental exploration towards a 26% efficiency rear-junction n-type silicon solar cell with front local-area and rear full-area polysilicon passivated contacts

Passivating contacts for high-efficiency silicon-based solar cells: From single-junction to tandem architecture

The 18.3% Silicon Solar Cells with Nano-Structured Surface and Rear Emitter

Interdigitated Back Contact Technology as Final Evolution for Industrial Crystalline Single-Junction Silicon Solar Cell

Mass production of industrial tunnel oxide passivated contacts (i‐TOPCon) silicon solar cells with average efficiency over 23% and modules over 345 W

Toward Efficiency Limits of Crystalline Silicon Solar Cells: Recent Progress in High‐Efficiency Silicon Heterojunction Solar Cells

Efficient Heterojunction Solar Cells on P-Type Crystal Silicon Wafers

N-type solar cells: advantages, issues, and current scenarios

Electrical Performance, Loss Analysis, and Efficiency Potential of Industrial‐Type PERC, TOPCon, and SHJ Solar Cells: A Comparative Study

Numerical study of mono-crystalline silicon solar cells with passivated emitter and rear contact configuration for the efficiency beyond 24% based on mass production technology

Further Efficiency Improvements of the N-Type MWT Si Solar Cells Using Industrial Processes

Passivating Contacts for Crystalline Silicon Solar Cells: An Overview of the Current Advances and Future Perspectives

Monolithic perovskite/silicon tandem solar cells with optimized front zinc doped indium oxides and industrial textured silicon heterojunction solar cells

Silicon heterojunction-based tandem solar cells: past, status, and future prospects

An industrially viable TOPCon structure with both ultra-thin SiOx and n+-poly-Si processed by PECVD for p-type c-Si solar cells

Application of n‐Polysilicon Rear Emitter for High‐Efficiency p‐TOPCon Solar Cells

Approaching 23% with large‐area monoPoly cells using screen‐printed and fired rear passivating contacts fabricated by inline PECVD

Industrial TOPCon solar cells on n-type quasi-mono Si wafers with efficiencies above 23%

Mass production of crystalline silicon solar cells with polysilicon‐based passivating contacts: An industrial perspective