Abstract:During the synthesis and processing of polymers, a significant amount of polymer may be deposited on the heat transfer surfaces. This study deals with the fouling behaviour of a vinyl acetate vinyl ester copolymer during emulsion polymerisation. The influence of the state of polymerization and the wall temperature was investigated. Experiments were performed in a 5 L reactor system combined with a flow channel. By using a fluidic heated or cooled flow channel it is possible to carry out investigations on heated or cooled surfaces. The deposition was quantified by the mass-based fouling resistance, by a gravimetric calculation of the fouling mass, the height of the fouling layer and the surface coverage using a digital microscope. It was shown that the state of polymerization and the temperature have a strong influence on the fouling behaviour, especially on the structure of the fouling layer. INTRODUCTION Emulsion polymerization is currently the preferred process for the commercial production of vinyl acetate, chloroprene, various acrylate copolymerization and copolymerization of butadiene with styrene and acrylonitrile (Odian, 2004). The polymerization process is frequently accompanied by the formation of deposits on the internal surfaces of the polymerization reactors (reactor wall, baffles, impeller). This deposition which occurs during the synthesis of polymers is referred to as polymerization fouling. The fouling layer on the heat-transferring surface forms an additional heat conducting resistance and reduces the efficiency of the heat exchanger. This increases the required heat transfer area for a given production capacity as well as the energy demand and thus ultimately increases CO2 emission. This study deals with polymerization fouling which forms during emulsion polymerization. A review of chemical reaction fouling, primarily of organic fluids, was given by Watkinson and Wilson (1997). Fouling during emulsification polymerization was recorded by Vanderhoff (1981). Here fouling is defined as coagulation of latex particles in consequence of instabilities. Because different substances and reactions may be involved during synthesis, there is no general knowledge of polymerization fouling (Bott, 1995). The deposition processes in general are still mostly unknown and there are only very substance-specific publications. Looking at the literature in the field of organic fouling, a major focus on auto-oxidation is found. Polymerization, on the other hand, has been given little consideration (Watkinson and Wilson, 1997). Buchelli et al. (2005) have investigated the fouling behavior of low-density polyethylene (LDPE) in a tubular reactor. The focus was on the determination of the fouling layer thickness in an industrial polymerization reactor based on plant data and heat transferring models. Tabrizi and Fadae (2017) addressed the applicability of two conductivity sensors for the investigation of fouling deposits during emulsion polymerization of different model material systems. Both studies deal with detection possibilities and less with the deposition mechanism itself. Cunningham and O'Driscoll (1991) investigated the conditions under which fouling occurs in tubular polymerization reactors using bulk methyl methacrylate polymerizations. They demonstrated that reactor orientation and flow direction have a significant effect on fouling behavior. Gottschalk et al. (2015) carried out initial investigations of a vinyl acetate-based copolymer. It was shown that fouling can be reduced by modifying the surface with diamond-like carbon coatings. All of these publications only deal with very specific influencing factors and resulting phenomena, but little work has been reported on the basics of the deposition mechanism. The purpose of this study is to obtain general information on polymerization fouling during emulsion polymerization of a vinyl acetate vinyl ester copolymer. For this purpose, four situations are defined in which polymer deposits can occur: during synthesis (polymerization fouling), during further processing of the already reacted polymer (polymer fouling), as well as on heated and cooled surfaces (Fig. 1). In particular, the comparison to polymer fouling is used to develop a broader understanding and to work out the special features of polymerization fouling. Fig. 1. Schematic classification of the addressed

Polymer Versus Polymerization Fouling: Basic Deposition Mechanisms During Emulsion Polymerization by the Example of a Vinyl Acetate and Versa 10 Copolymer

Polymer Versus Polymerization Fouling: Basic Deposition Mechanisms During Emulsion Polymerization by The Example of A Vinyl Acetate And Versa® 10 Copolymer

INVESTIGATION OF THE FOULING BEHAVIOUR OF A POLYMER DURING SYNTHESIS

The Polymer-rich Phase Solidification Process of PVDF-PVP-DMAc-H2O Solution

Mechanism and kinetics of emulsion copolymerization of vinylidene chloride—Critical conversion at the end of interval 2 and rate of polymerization

Fouling During Polymerization in Different Continuous Reactor Setups

Study on Kinetics of Vinyl Acetate/VeoVa 10 Emulsion Copolymerization

Surface modification of poly(vinyl alcohol) fibers to control the fiber-matrix interaction in composites

Mass Transfer in Emulsion Polymerization: High Solids Content Latex and Mixing Effects

Dewetting of Polymer Films with Built-In Topographical Defects

Kinetics of Vinylidene Chloride / Acrylonitrile / Styrene Suspension Polymerization

Influence of Suspended Emulsion Polymerization Conditions on Particle Characteristics of Polyvinyl Chloride Resin

Mini-emulsion formation and polymerization of styrene

Free-radical crosslinking polymerization and copolymerization of multivinyl compounds

Effects of Polymers on the Structure and Deposition Behavior of Waxy Oils

Emulsion Polymerization of 2-Methylene-1,3-Dioxepane and Vinyl Acetate: Process Analysis and Characterization

Synthesis of Well-Defined Poly(vinyl alcohol- co-vinyl acetate) Copolymers by Alcoholysis of Poly(vinyl acetate) Synthesized by Macromolecular Design via Interchange of Xanthate Polymerization, and Their Use as a Stabilizer in Emulsion (Co)polymerization of Vinyl Acetate

Physico-chemical study of polymer mixtures formed by a polycation and a zwitterionic copolymer in aqueous solution and upon adsorption onto negatively charged surfaces

Kinetic Investigation of the Emulsion Polymerization of Vinylidene Fluoride

Towards natural care products: structural and deposition studies of bio-based polymer and surfactant mixtures

Understanding the emulsion copolymerization kinetics of vinyl acetate and vinyl silanes