The Polymer-rich Phase Solidification Process of PVDF-PVP-DMAc-H2O Solution

LU Yin,ZHANG Lin,CHEN Huan-lin,LI Bo-geng

DOI: https://doi.org/10.3321/j.issn:1003-9015.2006.04.002

2006-01-01

Abstract:The solidification mechanism and rate of PVDF-PVP-DMAc-H2O membrane-casting solution were investigated. The differential scanning calorimeter (DSC) and the X-ray powder diffractometer (XRD) were used to analyze the properties of PVDF polymer gelation. It is found that the solidification process conversing from polymer solution to polymer gel is a physical-reversible process caused by crystallization, and the crystalline solid-liquid phase separation happens under the nucleation and growth mechanism. During the conversion process from polymer solution to polymer gel, the fluidity of the PVDF-PVP-DMAc-H2O system was detected by the falling-ball experiment. At the gelation point, the transformation process of fluid to solid takes about 2.5 to 4 minutes. The phase separation rate during the membrane formation process was measured by the light transmission method. The liquid-liquid phase separation happens at about 1 minute after the gel demixing. There is about 1.5~3 minutes left for the morphological variation between the polymer-rich and polymer-lean phase before the solidification of the polymer-rich phase, and it is the key period for the formatin, variation and finalization of the pores in the membrane.