Abstract:In this study, a 780 MPa grade ferritic-bainitic dual-phase steel with excellent matching of strength-plasticity and formability was developed using thermomechanical control processing. Optical microscopy, Scanning electron microscopy, and Electron Backscatter Diffraction techniques were used to characterize the microstructure comprehensively, and the effects of coiling temperature on the microstructure, the strength-plasticity, and hole-expansion ratio of the test steels were thoroughly investigated. The results showed that the test steel had an excellent combination of ferrite and bainite at the coiling temperature of 520 °C, 23.7 and 76.3%, respectively, with a hole expansion ratio of 58.5 ± 2.8%. The uniformity of the microstructure was the key to obtaining a high expansion ratio in ferrite-bainite dual-phase steels. The test steels formed granular bainite at low-temperature coiling, while polygonal ferrite was promoted at high-temperature coiling. The effect of coiling temperature on grain size is small. Dislocations were redistributed during high-temperature coiling, resulting in a decrease in dislocation density. The higher elongation and hole expansion rate at higher coiling temperatures were attributed to increased polygonal ferrite content, reduced grain size, and enhanced TRIP effect. When coiling at low temperatures, the agglomeration of polygonal ferrite or granular bainite tends to result in a non-uniform distribution of the soft and hard phases of the matrix. At the same time, the strong texture parallel to the rolling direction has a significant difference in plasticity in different directions, leading to non-uniform deformation, which is liable to stress concentration, causing crack nucleation and extension in the hole expanding process, thus reducing the hole expansion performance.

Effect of elasto-plastic compatibility of grains on the void initiation criteria in low carbon steel

Achieving High Strength and High Ductility in Nanostructured Metals: Experiment and Modelling

Effect of hardness of martensite and ferrite on void formation in dual phase steel

Effect of Strain Localization on the Mechanical Properties from Nonuniform Grain Size Distribution of Ultralow Carbon Steel

Effect of Inclusions and Microstructural Characteristics on the Mechanical Properties and Fracture Behavior of a High- Strength Low- Alloy Steel

The effect of void defect on the evolution mechanisms of dislocations and mechanical properties in nickel-based superalloys by molecular dynamics simulation of real γ/γ′ structures

The mechanistic origins of heterogeneous void growth during ductile failure

Effect of Carbon in Severe Plastically Deformed Metals

Effect of grain ultra-refinement on microstructure, tensile property, and corrosion behavior of low alloy steel

Experimental and FE analysis of void closure in hot rolling of stainless steel

On the effect of strain and triaxiality on void evolution in a heterogeneous microstructure -- A statistical and single void study of damage in DP800

Influence of Prior Austenite Deformation and Non-Metallic Inclusions on Ferrite Formation in Low-Carbon Steels

Effect of grain orientation and local strains on void growth and coalescence in titanium

Effect of Coiling Temperature on Microstructure and Properties of Ferritic-Bainitic Dual-Phase Steels

Effect of Grade on Thermal–Mechanical Behavior of Steel During Initial Solidification

Model of Void Nucleation on Grain Boundaries in Dynamic Failure of Ductile Metals Incorporating Interface Incompatibility

Effect of Hot Coiling Under Accelerated Cooling on Development of Non-equiaxed Ferrite in Low Carbon Steel

Effect of Grain Size on the Plastic Deformation Behaviors of a Fe-18Mn-1.3Al-0.6C Austenitic Steel

Revealing the Void Formation Mechanism during Superplastic Deformation of a Fine-Grained Ni–Co-Base Superalloy

Effect of Random Void Defects on the Mechanical Behavior of C/C Braided Composites

The Netted Ferrite at Grain Boundaries in the Steels with Thermomechanical Processing