Effect of carbon alloying on microstructure and mechanical behaviors of Fe35Ni35Cr20Mn10 multi-component alloy
Jun Zhou,Tinghui Jiang,Hengcheng Liao,Hao Chen,Jiwei Zheng,Weijun Zhu
DOI: https://doi.org/10.1016/j.matchar.2022.111934
IF: 4.537
2022-04-01
Materials Characterization
Abstract:The effect of carbon-alloying on the microstructure and mechanical behaviors of Fe35Ni35Cr20Mn10 multi-component alloy (MCA) was studied by microstructure characterization and tensile test. In as-cast (Fe35Ni35Cr20Mn10)98.5C1.5 MCA, M23C6-type carbide (M = Cr, Fe, Ni, Mn; more Cr contained) formed at the grain boundaries has a coherent relationship with the FCC matrix. After a homogenization treatment at 1000 °C for 12 h, the carbide phase formed during the solidification course becomes coarsened and rounded by partially re-dissolving, and, at the same time, a great number of blocky M23C6-type particles (about 50–200 nm) are coherently precipitated in a large area around the grain boundaries. In as-homogenized state, carbon-alloying induced fine-grain strengthening, solution strengthening and coherent precipitation hardening of nano carbide particles greatly increase the yield strength from 198 MPa to 480 MPa. The carbon-alloying induced grain refinement and coherent precipitation of nano carbide particles and the formation of dislocation cells and deformation twins during the tensile deformation are thought to be responsible for the high plasticity of (Fe35Ni35Cr20Mn10)98.5C1.5 MCA (28.3% in elongation). Microstructure evolution at different strain stages and the working hardening rate curves demonstrate that addition of carbon in Fe35Ni35Cr20Mn10 MCA system increases the critical stress for the formation of deformation twinning and thus increases the stacking fault energy.
materials science, multidisciplinary,metallurgy & metallurgical engineering, characterization & testing