TiO2–LiF composite coating for improving NCM622 cathode cycling stability: one-step construction

Kai Huang,Jinxia Zhou,Huili Yang,Tianzheng Xie,Tu Lan,Suichang Ong,Heng Jiang,Yibo Zeng,Hang Guo,Ying Zhang

DOI: https://doi.org/10.1039/d3ra05659g

IF: 4.036

2023-11-21

RSC Advances

Abstract:The Ni-rich NCM622 is a promising cathode material for future high energy lithium ion batteries, but unstable electrochemical performance of NCM622 hinder its large scale commercial application. The cycling peformance of nickel-rich LiNi 0.6 Co 0.2 Mn 0.2 O 2 (NCM622) cathode materials can be improved by surface coating. Here, a one-step approach based on TiF 4 is used to successfully manufacture modified NCM622 cathode materials with a TiO 2 –LiF coating. The TiO 2 –LiF coated NCM622 preserves 79.7% capacity retention which is higher than the pure NCM622 (68.9%) at 1C after 200 cycles within 2.7–4.3 V. This material serves as the cathode for lithium-ion batteries (LIBs). The uniform TiO 2 –LiF coating layer can alleviate structural degradation brought on by unfavorable side reactions with the electrolyte has been validated. TiO 2 –LiF coated on NCM622 cathode materials can be modified easily by one-step approach.

chemistry, multidisciplinary

What problem does this paper attempt to address?

The problem this paper attempts to address is improving the cycling stability of high-nickel-content NCM622 cathode materials in lithium-ion batteries. Specifically, although high-nickel-content NCM622 cathode materials have the advantages of high specific capacity and low cost, their electrochemical performance is unstable. This instability is particularly evident at high charging voltages, where irreversible phase transitions occur, leading to surface structure damage. Additionally, adverse side reactions between NCM622 and the electrolyte, such as the formation of a cathode electrolyte interface (CEI) and the dissolution of transition metal ions, also reduce the active components and reversible capacity. These issues limit the large-scale commercial application of NCM622.

To address these problems, the authors propose a one-step synthesis technique based on TiF4, successfully preparing NCM622 cathode materials with a TiO2–LiF composite coating. Through this method, the coating can effectively mitigate adverse side reactions between the electrolyte and NCM622, thereby improving the material's cycling stability and electrochemical performance. Experimental results show that after 200 cycles, the NCM622 with the TiO2–LiF coating maintained a capacity retention rate of 79.7% within the voltage range of 2.7–4.3 V, significantly higher than the uncoated NCM622 (68.9%). This indicates that the TiO2–LiF composite coating has a significant effect on improving the cycling stability of NCM622 cathode materials.